1. Properties of FRP pultruded profiles
A. High strength
FRP is stronger than structural steel on a pound-for pound basis. It has been used to buildings, walkway, sub-floors and platforms.
B. Light weight
FRP is 20-25% the weight of steel and 70% the weight of aluminum. FRP are easily transported, handled and lifted into place. Total structures can often be preassembled and shipped to the job site ready to installation.
C. Anti-corrosion
FRP will not rot and are impervious to a broad range of corrosive elements. This feature makes FRP a natural selection for indoor or outdoor structures in pulp and paper mills, chemical plants, water and sewage treatment plants, structural near salt water and other corrosive environments.
2. Pultruded Flat Bars are manufactured with the pultrusion process after choosing the correct raw materials major including the resin, fibers and additives according to the profiles requirement including mechanical strength, electrical insulation, anti-corrosion etc.
3. Pultruded Flat Bars can meet the customer's requirements by using different combination of resin, fibers and others.
4. Pultruded Flat Bars offer a unique combination of chemical resistance, size stability, high strength, and thermal/electric non-conductivity, etc.
5. Pultruded Flat Bars are widely used for chemical processing, oil and gas, electrical and utility, wastewater treatment, transportation, construction etc.
Pultrusion Section Bar Function Exponent | |||
(Property) | Test Method | Units | Mean-Value LC/CW |
Tensile Strength | ASTM D638/GB1447-83 | MPa | 210/75 |
Tensile Modulus | ASTM D638/GB1447-83 | GPa | 22/10 |
Tensile Strength | ASTM D790/GB1449-83 | MPa | 302/76 |
Flexural Modulus | ASTM D790/GB1449-83 | GPa | 18.6/7.2 |
Compressive Strength | ASTM D695/GB1448-83 | MPa | 258/98 |
Compressive Modulus | ASTM D695/GB1448-83 | GPa | 19.2/7.2 |
Interlaminar Shea(LW) | ASTM D2344/GB3357-82 | MPa | 24.5 |
Charpy Impact Strength | ISO 179/GB1451-83 | KJ/sqm | 279 |
Barcol Hardness | ASTM D 2583 | ------- | 50 |
Elongation to Break | ASTM D 638/GB1447-83 | % | 0.9 |
Water Absorption | ASTN D 570/GB1462 | % | 0.57 |
Density | ASTM D792 | g/cm | 1.8 |
Coefficient of Thermal Expansion | ASTM D696/GB2572-82 | 10-6./°C | 5.1 |
Flammability Classification | UL94/GB8924-88 | ------- | VO(32) |
Tunel Test | ASTM E-84 | ------- | 25Max |
Flammability Extinguishing | ASTM D 635 | ------- | selfextinguishig |
Arc Resistance(LW) | ASTM D 495/GB1411-78 | sec/(s) | 120 |
Dielectric Constant(PF) | ASTM D 150/GB1409-79 | @60HZ | 5 |
Dielectric Strength (PF) | ASTM D 149/GB1408-78 | KV/mm | 8 |
Dielectric Strength(LW) | ASTM D 149/GB1408-78 | KV/mm | 1.6 |
Surface Resistance | ASTM D 257/GB1410-78 | Ω | 10-10 |
Volume Resistance | ASTM D 257/GB1410-78 | Ω.cm | 10-10 |
Remarks: LW-lengthwise CW-crosswise PF=Perpendicular to laminate face |