Guangzhou low price low temperature carbon steel welding rod ( E6013)

1.Size: 2.5mmX300mm, 3.2X300mm, 4.0X400mm2.Materials:Low carbon steel

3.Packing: 2.5kg/box 8box/carton ; 5kg/box 4box/carton or as your requirement.

4.Surface: With green or grey color titanium coated

Application for low temperature carbon steel welding rod ( E6013)

1.Application: For important mild steel stucture and low steel with low strenght.

2.Welding of low carbon steel structure, especially suitable for sheet small and short weld discontinuities

4.Surface: with red, green ,grey color coated

Features of low temperature carbon steel welding rod ( E6013)

1.Welding electrodes e6013 is a kind of carbon steel electrode with iron powder low-hydrogen potassium type coating.

2.. It has stable arc, fewer spatters, good slag detachability and excellent welding performance.

3.The deposited metal has excellent mechanical properties. All-position welding.

deposited metal:

Use Note : Electric shock can kill. Do not permit electrically live parts or electrodes to contact skin,

clothing or gloves if they are wet. Insulate yourself from work and ground.

FUMES Fumes and gases can be dangerous to your health. Keep fumes and gases away from your breathing zone and general area. Keep your head out of fumes... Use enough ventilation or exhaust at the arc or both.

Specfication Of low temperature carbon steel welding rod ( E6013)

Main information
Power:AC,DC/electrode negative or positive
Standard(mm)		Current Range(A)
Diameter	Length	Downward Welding	vertical up welding
2	250	30-50	20-40
2.5	300	60-100	50-90
3.2	350	100-140	90-120
4	400	140-190	120-170
5	400	190-250	140-210

Deposited metal chemical compositions(%)
C	Mn	Si	S	P
≤0.12	0.30-0.60	≤0.25	≤0.035	≤0.040

Deposited metal mechanical property

Text Items	Rm(Mpa)	Rel(Mpa)	A(%)	KV2(J)
Guarantee Value	≥420	≥330	≥22

Item Name:	Electrodes Welding Rods E4303
Length:	300-400mm
Diameter	2.5-5.0mm
Material	H08A
Characteristic	Especially suitable for sheet metal welding, tack welding and other types of welding which require a smooth and clean bead appearance.
Production capacity	300ton/month
Delivery time	15--30days
Packaging	normal packing or as your specific requirements