Compound Geomembrane

Description

Compound geomembrane is a waterproof material formed with the fusing of non woven fabric 

and Polyethylene membrane. Compound geomembrane may be of two types - one side non woven 

fabric and one side PE membrane and two sides non woven fabric with PE membrane in between.

Geomembrane Material:PE

Geotextile Material:PP or PET staple nonwoven geotextile

                PET filament spunbond nonwoven geotextile

Features

1.High tensile strength & tearing resistance

2. High bursting resistance

3.Aging resistance

4.Anti-corrosion

5.Long temperature range and life span

Application

The gemenbrane is against drawing, tearing resistance, and high CBR plunger strength, can 

meet the need of civil engineering such as water conservancy, municipal administration, building, 

traffic, subway, tunnel ect. Because of selecting high polymer for use and adding the aging-resistant materials in the production technology, it can use in the unconventional temperature 

environment. 

Mass per unit are g/m2

400

500

600

700

800

900

1000

Marks

Thickness of membrane
mm

0.25-0.35

0.3-0.5

Tensile at break kN/ m

5

7.5

10.0

12.0

14.0

16.0

18.0

MD/CD

CBR strength kN

1.1

1.5

1.9

2.2

2.5

2.8

3.0

Tear strength kN

0.15

0.25

0.32

0.40

0.48

0.56

0.62

MD/CD

Note: According to the specifications of thickness per unit area, the actual specifications in the range of 

specifications between the adjacent table, according to the interpolation method to calculate the appropriate 

evaluation indicators; beyond the scope of the table, the assessment indicators to be negotiated by the supply and 

demand.

Thickness of membrane
mm

0.2

0.3

0.4

0.5

0.6

0.7

0.8

Note

One textile one membrane mm

   0.4

   0.5

   0.6

   0.8

   1.0

   1.2

   1.4

Two textile one  membrane mm

  0.5

   0.6

   0.8

   10.

   1.2

   1.4

    1.6