HDPE textured geomembrane
Negotiable
Min.Order:1
Zibo Evergreen Trading Co., Ltd.
Textured geomembrane is a premium grade linear high density polyethylene (HDPE) geomembrane liner that has a textured surface on one or both sides of the liner. It is a coextruded, textured liner, with the textured surface as an integral part of a three layer co-extruded geomembrane sheet. Our textured geomembrane is available with width lor can be customerized.
Tech date attached
High Density Polyethylene (HDPE) Geomembrane - TexturedProperties | Test Method | Test Value | Testing Frequency (minimum) | ||||||
0.75 mm | 1.00 mm | 1.25 mm | 1.50 mm | 2.00 mm | 2.50 mm | 3.00 mm | |||
Thickness mils (min. ave.) lowest individual for 8 out of 10 values lowest individual for any of the 10 values | D 5994 | nom.(-5%) -10% -15% | nom.(-5%) -10% -15% | nom.(-5%) -10% -15% | nom.(-5%) -10% -15% | nom.(-5%) -10% -15% | nom.(-5%) -10% -15% | nom.(-5%) -10% -15% | per roll |
Asperity Height mils (min. ave.) (1) | GM 12 | 0.25 mm | 0.25 mm | 0.25 mm | 0.25 mm | 0.25 mm | 0.25 mm | 0.25 mm | every 2nd roll (2) |
Density (min. ave.) | D1505 /D 792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 90,000 kg |
Tensile Properties (min. ave.) (3) yield strength break strength yield elongation break elongation | D 6693 Type IV | 11 kN/m 8 kN/m 12% 100% | 15 kN/m 10 kN/m 12% 100% | 18 kN/m 13 kN/m 12% 100% | 22 kN/m 16 kN/m 12% 100% | 29 kN/m 21 kN/m 12% 100% | 37 kN/m 26 kN/m 12% 100% | 44 kN/m 32 kN/m 12% 100% | 9,000 kg |
Tear Resistance (min. ave.) | D 1004 | 93 N | 125 N | 156 N | 187 N | 249 N | 311 N | 374 N | 20,000 kg |
Puncture Resistance (min. ave.) | D 4833 | 200N | 267 N | 333 N | 400 N | 534 N | 667 N | 800 N | 20,000 kg |
Stress Crack Resistance (4) | D 5397 (App.) | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | per GRI GM10 |
Carbon Black Content (range) | D 1603 (5) | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 9,000 kg |
Carbon Black Dispersion | D 5596 | note (6) | note (6) | note (6) | note (6) | note (6) | note (6) | note (6) | 20,000 kg |
Oxidative Induction Time (OIT) | D 3895 D 5885 | 100 min. 400 min. | 100 min. 400 min. | 100 min. 400 min. | 100 min. 400 min. | 100 min. 400 min. | 100 min. 400 min. | 100 min. 400 min. | 90,000 kg |
Oven Aging at 85°C (7),(8) | D 5721 D 3895 D 5885 | 55%
80% | 55%
80% | 55%
80% | 55%
80% | 55%
80% | 55%
80% | 55%
80% | per each formulation |
UV Resistance (9) | GM11 D 3895 D 5885 | N.R. (10) 50% | N.R. (10) 50% | N.R. (10) 50% | N.R. (10) 50% | N.R. (10) 50% | N.R. (10) 50% | N.R. (10) 50% | per each formulation |