15000 M3/Year AAC Block Making Plant :

Autoclave aerated concrete block machine:

AAC Machine is horizontally set, the cover is made of a 16mnr steel plate, the flanges used in the cover and body of the machine is forged from a 16mn steel bar. Strict non-destructive Testing and heat treatment should be performed to the welding lines in the pressure sustaining parts according to relevant specifications.

Features:

1 .Product weight is according to 600 kg/m3 to control.

2 .Annual capacity 200,000M3.

3 . Set raw material proportion: cement 6.5%, raw lime 23%, fly ash 68%, gypsum 3%, aluminum paste powder 350g/M3.

4 .Water and material rate 0.631

5 .One mould product 2.88M3

6 .Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.

7.Casting slurry temperature 38-42 degree

8 . body quiet stop. Time is 1.5-2.5housr, temperature 50-90 degree, after quiet stop body strength is 0.15-0.18Mpa

9 .Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.

Specification:

Cement lime fly ash style aerated block raw material proportion

11.  Cement lime Sand style aerated block raw material proportion

Our factory is professional manufacturer of autoclaved aerated concrete (AAC) plants for more than 10 years, and we can supply complete set of autoclaved aerated concrete plant withcapacity of 50 000m³, 100 000 m³, 150 000 m³, 200 000 m³, 250 000 m³, 300 000 m³annually, including plant design, equipments installation, technical support, personal training, etc, and also can design and manufacture as per clients' requirement and so on.

Raw materials: cement, lime, sand (or fly ash), gypsum, aluminum powder, water.