spot welding pure tungsten electrode

WT20 

Thoriated Tungsten is the most commonly used tungsten in America and some other countries and is a good general use tungsten. Especially, it performs well when overloaded with extra amperage. However,since it is a low-level radioactive hazard many users have switched to other alternatives. This tungsten is used primarily for DC welding of carbon & stainless steels, nickel alloys and titanium,etc..

Wce

Ceriated Tungsten is a non-radioactive material.

It is very widely to be used for the welding of orbital tube, pipe, very small parts, short welding cycles and also where a specific number of welds are called and then the electrode is to be replaced.

It is known to be especially good for DC welding with low amperage because it starts very easily at low amps and usually requires about 10% less amps to operate than thoriated material. 

WL

Lanthanated Tungsten is a non-radioactive material with good welding performance. 

In Europe , Lathanated Tungsten has been the most popular alternative to 2% Thoriated Tungsten for most applications. This tungsten is used primarily for DC welding but will also show good results for AC welding.

Its electric conductivity is most closed to that of 2% Thoriated Tungsten. Welders can easily replace Thoriated Tungsten Electrodes with Lanthanated without any changes of welding program. 

WZ

Zirconiated Tungsten has good performance in AC welding. It balls up well in AC welding and has a more stable arc than pure tungsten. Especially with excellent performance in high load AC welding, it is not replacable by any other electrodes. It also resists contamination well in AC welding. Zirconiated Tungsten is most commonly used for AC welding of aluminum and magnesium alloys.

WP

Pure Tungsten , the least expensive of all tungsten electrodes, is generally used in the AC welding of aluminum and magnesium alloys

WY

Yttriated Tungsten is primarily used in military and aviation industry with narrow arc beam,high compressing strength,highest welding penetration at medium and high current.