High Temperature Anti-wear Paste For Mould Ejector Pin
Stand 1400 high temperature
No Melting
No Flow out
No carbonization

Description

High Temperature Anti-wear Paste For Mould Ejector PinA white non-carbonized-under-high-temperature lubricating paste for lubrication of all kinds of surfaces subject to high load, particularly operation at low speed and/or oscillating motion and of steel and non-ferrous metal screw ,plug and bayonet joints. 

 

Applications

-Anti-Selzlng non-destructive disassembly of threaded conncetions subject to high temperatures, i.e. at internal combustion engines and turbines oven after long service time.

-Corrosion protection for nuts and bolts,sockcts and spindles in refurenes, steel-and cement mills, marine and agriculture.

 

 

Benefits

-Best use-ONE single paste for MANY applications;

-White-coloured, non-staining, outstanding lubricity 

-High pressure, low friction and low wear resistance, reliable anti-serze effect and corrosion protection.

-Economical and ecological solution for many plants and shops which have been depending on a number of special pastes so far.

-contains organic active molybdenum additive for increased performance.

 

Environment

Ecology - FUKKOL H.T PASTE is non-toxic,contains no ferrous metals and is free from graphite , molybdenum-disulphide and sulphide additives.

 

 

Typical physical properties 

Appearance	White color		Base oil	Synthetic oil compound with organic thickener and combination of white solid lubricants
Unworked penetration	280-320
Specific gravity	1.2g/cc at 20°C
Dropping point	None		Base oil viscosity		21mm2/s at 40°C
Temperature range	-40°C~+1400°C		Friction value		0.10-0.13
Degree of corrosion	1-90		Depth  of wear		0.3um
Salt spray test	>500 hours		Four-ball tester(VKA)		3800/4000N