High Manganese Plate X120Mn12/Mn13
1)Good Ductility
2)High Wear Resistance
3)Excellent Impact Toughness
4)High Hardness

High Manganese Plate X120Mn12 Hot Rolled Plates From Testeel

1.Characteristics of products

abrasive resistance steel
Strong plasticity and impact toughness
It is work hardening steel - the more impact and abrasion it gets the harder the surface becomes.
Steel stays ductile underneath - only surface layer hardens.
With continued impact steel can harden to 500HB above.
When rolled - never brittle.
Low friction properties.
Non-magnetic.

2.Standard-GB, ASTM, JIS, DIN

-American standard- ASTM A128

-Europe standard- X120Mn12

-JIS- SCMnH11

-China national standard- GB Mn13

- DIN- 1.3401

3.Brand name- Baosteel

4.Corresponding foreign brands

JIS- SCMnH11, AFNOR- Z120Mn12, DIN- 1.3401,EN- X120Mn12,ASTM-A128

5. Chemical composition(%)

Brand	C	Si	Mn	P	S
X120Mn12	0.90-1.20	0.30-0.80	12.00-14.00	≤0.035	≤0.030

6. Mechanical Properties

Tensile Strength	Elongation	20°C Impact Resistance	Initial Hardness(HB)	Hardness after Hardened(HB)	180°old Bending Test
≥900MPa	≥40%	ak≥50(J)	190-250	≥300	Qualified

7.Specifications of Product

2-5mm x 1000 x 2000mm

6-20mm x 1000-2500mm x 3000 or above