Product Details

Low Carbon Steel Wire

1. Wire Rod(low carbon steel, ISQ195, ASTM,SAE 1006/1008)

2. Wire Drawing(draw 6.5mm wire to 4.mm or other diameter, two types of drawing methods)

3. Annealing(wire go through the high temperature, improve T/S, preparation for the zinc coating)

4. Zinc coating(electro GI wire and hot-dipped GI wire, dealed with electro polish and high temperature. More zinc coating, the better resistance of corrosion)

5. Wire Coiling(Weight of coil/roll: 200kg, 100kg, 50kg, 25kg, 10kg, 2-8kg)

2. Specification

Wire diameter: 1.2mm-20mm

Yield strength: 195-235Mpa

Tensile strength: 295-540 Mpa or 350-680 N/MM2

Elongation rate: 18-25%

Zinc coating: first grade(18-30g/m2),second grade(12-18g/m2),third grade(9-12g/m2)

Zinc coating determine the resistant to corrosion.

3.Chemical Composition

Type	Grade	Chemical Composition(&)
		C	Mn	Si	S	P
				≤
Q195	1	0.06-0.12	0.25-0.50	0.30	0.050	0.045

Type	Q235				Standard NO.			GB 700-88
Chemical Composition%	C	Mn	Si		S	P	Cr			Ni	Cu
	0.14-0.22	0.30-0.60	0.30		0.050	0.045	0.30			0.30	0.30
Shape	Ingot,blank,profile,bar,plate,tube,strip line
Specification	Tensile strength(Mpa)			Yield strength(Mpa)					Elongation rate(%)
	375-460			185-235					21-26 as varied sizes