cold/hot rolled 1.0mm aisi 304 2B stainless steel sheet/plate made in China

Product Description

Independent warehouse & factory
Quick delivery (within 3 days)
Best service
High quality with reasonable price
High efficiency
Good reputation
Samples can be provided as your requirements.

Introduction

aisi 304( 18Cr-8Ni ) stainless steel is one of Austenitic stainless steel. As a versatile steel,

it has good corrosion resistance, heat resistance, low temperature strength and

mechanical properties. Meanwhile, it is quite good in pressing, bending and other

thermal processing.No heat harding and non magnetic

chemical properties

Typical chemical composition
%	304	304L	310s	321
C	0-0.07	0-0.03	0.8	0.08
Mn	0-2.0	0-2.0	2.00	2.00
Si	0-1	0-1	1.00	1.00
P	0-0.05	0-0.05	0.035	0.035
S	0-0.02	0-0.02	0.030	0.03
Cr	17.5-19.5	17.5-19.5	24.0-26.0	17.0-19.0
Ni	8-10.5	8-10.5	19.0-22.0	9.0-12.0
Mo
TI				5×C%
Fe	Balance	Balance

Pysical properties

Tensile strength σb (MPa) ≥ 520

Conditions yield strength σ0.2 (MPa) ≥ 205

Elongation δ5 (%) ≥ 40

Section shrinkage ψ (%) ≥ 60

Hardness: ≤ 187HB; ≤ 90HRB; ≤ 200HV

Our Services

Stainless Steel Sheet:
Our sheet are directly ordered from mills.300 series stainless steel(aisi 304,aisi 3 04L,aisi 316L,aisi 321),duplex(2205),heat resistant steel(309s,310s)are the main product.Thickness from 0.2mm to 20mm,width is from 300mm to 2000mm,weight is from 2 tons to 26 tons.
The chemical and mechanical composition of the material is in accordance with GB,JIS,ASTM,and EN.

aisi 304 2B stainless steel plate/sheet :

aisi 304 2B stainless steel plate /sheet :

aisi 304 2B stainless steel plate/sheet :

Stainless Steel Plates/sheets:

Hot rolled stainless plate/sheet products are both cut to length and plant rolled plate/sheet.
Thickness:0.3mm-100mm
Size:1500*3000mm,1500*6000mm,1000*2000mm,1800*6000mm,2000*6000mm or as request.

aisi 304 2B stainless steel plate/sheet :

Processing:
There are high-tech equipments to processing stainless coils and sheets/plates with skilled workers.