Appearance :

No color semi-transparent film 

solubility:

Insoluble in water

Melt index:

7±2/10min;150℃

Melt point:

45-102℃

Grame weight:

11.4g/mP2P/0.01mm

Washing resistance:

good

Strip temperature:

<-30℃

Lamination strength:

>2.2kgf/cm

High temperature resistance:

≤0mm                  (HGT2815-1996 90℃ 182g)

Alkali resistance:

≥2kgf/cm               (10%NaOH solution  24h)

Hydrolysis resistance:

≥2kgf/cm               (70℃,95%RH   24h)

Yellowing resistance:

4 level                   (HGT3689-2011 A method 24h)

Suggestion operation condition: 

Press machine

0.4~0.6Mpa,110~130℃, 8~20s

Compounding machine

0.4~0.6Mpa, 120~150℃

Note:1. Intensity selection of0.2mm thick film, the use of space leather with three layers of cloth, pressing machine,0.4Mpa,150℃,20s test, difference of fabric material and peel data.

           2,have something with fabrics materials and thickness etc.