Specifications

virgin PP/Polypropylene
1.Appearance: Transparent,White
2.Virgin or recycld granules
3.Free sample, fast delivery
4CIQ SGS

 

 

2. Grade: Film grade, Injection molding grade, Extrusion grade, Pipe grade, Yarn grade, Raffia grade, Fiber grade, Homopolymer, Copolymer, Random Copolymer

 

 

3.Properties: polypropylene granule has the advantages of excellent comprehensive properties, good chemical stability, good shape processing performance and relatively low cost. PP polypropylene can adapt to a wider range of application requirements through modifying, copolymerization, grafting, blending, reinforced filling, transparency, filling, weather resistance.

 

 

4. Specification:

 

Properties	Unit	Test method	Value
Melt Flow Rate
Melt flow rate(230°C/2.16KG)	g/10min	ISO 1133	12
Mechnical Properties
Tensile modulus of elasticity(v=1mm/min)	Mpa	ISO 527-2	1550
Tensile yield at stress(v=50mm/min)	Mpa	ISO 527-2	35
Tensile yield at strain (v=50mm/min)	%	ISO 527-2	8
Tensile strain at break (v=50mm/min)	%	ISO 527-2	>50
Charpy impact strength unnotched(+23°C)	kJ/m2	ISO 179/1eU	110
Charpy impact strength notched(+23°C)	kJ/m2	ISO 179/1eA	3.0
Izod Impact strength notenched(+23°C)	kJ/m2	ISO 180/1A	3
Ball indentation hardness(H 358/30)	Mpa	ISO 2039-1	78

 

 PP Copolymer 

Tests	Value	Unit
Melt Flow Rate	45	g/10min
Density	0.90	G/cm3
Elongation Stress	10	%
Flexural modulus	14	Mpa
Rockwell hardness	95	R scale
IZOD impact strength	6.5	kg.cm/cm
Vicat softening point	152	°C
Heat distortion temperature	125	°C

 

5. Application: 

 

1)Injection: valve, fittings, crates, automotive, closure, appliances, kettles, food containers, housewares, toys, non-prefilled syringe.

2)Extrusion: thick sheet, sheet, pipe, straw, strapping, Stationery sheet, BOPP Film, thin sheet, band.

3)Blow Molding: bottles.

4)Thermoforming: tray, bowl, jelly cup, water cups.

5)Flat yarn: woven bag, jumbo bag, carpet.

6)Fiber: multifilament, carpet, Spundbond, non-wovens.

7)Film: Cast film (CPP), Blown film (IPP).

 