Product Details

Physical Properties:

1) Compressive strength

Direction	200 MCI	400 MCI
A (minimum)	15.0 MPa	15.0 MPa
B (minimum)	1.5 MPa	1.5 MPa
C (minimum)	0.2 MPa	0.2 MPa
Specimen dimensions Φ25.4 mm, length 25.4 mm from direction A, B and C, where A direction: parallel to passageways B direction: perpendicular to passageways and parallel to passageway walls C direction: perpendicular to passageways and 45% to passageway walls Speed: 1mm/min

2) Porosity/water absorption

Item	200 MCI	400 MCI
Minimum	18.6%	17.8%
Maximum	23.4%	20.7%
Average (n>5 per lot)	22.1%	19.6%
Total pore volume	0.18-0.24 (cm3/g)	0.18-0.24 (cm3/g)

3) Bulk density

100 MCI	0.46 g/cm3±15%
200 MCI	0.43 g/cm3±15%
300 MCI	0.50 g/cm3±15%
400 MCI	0.48 g/cm3±15%

4) Coefficient of Thermal Expansion

Item	200 MCI	400 MCI
Heating rate	5C/min, 20C…1000C	5C/min, 20C…1000C
Average	1.5*10-6K-1	1.8*10-6K-1

5) Thermal Conductivity

1.5…1.6 W/mk at temperature 25C…600C

6) Specific Heat Capacity

At:100C/200C/300C
800KJ/Kg950KJ/Kg2000KJ/Kg

7) Continuous High Temperature Durability

Maximum shrinkage of length after 100 hours at 1200C
200MCI 400MCI
Maximum:0.5% 0.1%

8) High Temperature Stability

Maximum shrinkage after 100 hours at 1450C
200 MCI400 MCI
Maximum2.0%2.5%

9) Gas Flow Resistance

Flow speed 16m/s200 MCI400 MCI
Pressure drop {10-2mmAg/mm} 60130

10) Structural Integrity to Thermal Shock

(Cooling with water)
Cracks start at approx. 800C
No destruction of ceramic bodies until approx. 1180C

11) Softening temperature

Definition: temperature, at which the instantaneous rate of thermal expansion is zero.

Procedure: analogous to coefficient of thermal expansion; determination with extrapolation.

Minimum: 1380C

Chemical Composition:

Item	Stoneware	Cordierite	Mullite- Cordierite	Mullite
SiO2	69~71	46~48	29~30	27~28
Al2O3	18~20	34~37	68~69	70~71
MgO	0.15~0.20	7.00~7.50	---	---
K2O.Na2O.CaO	3.00~3.30	2.50~2.90	0.70~0.90	0.80~1.20
Fe2O3	0.70~0.90	0.70~0.90	0.50~0.70	0.50~0.

We promise to reply you in 24hours, OEM & ODM service for your unique idea with absolute convenience. We value our business credit, promise to keep your company information confidential.If any inquiry or problem.Please feel free to contact with me.

Grace Zhang

Whatsapp/TEL:008613767885030

QQ: 84781705

Skype: yakegrace

Wechat: xz9426

TM: cn1000900349

Our Services

Q: What is your MOQ?

A: Our product MOQ is 1000kg&1m³

Q: What is the delievery time?

A: It takes aroud 10-15days for one 20" container.

Q: What is the shipping port?

A: Shanghai,Shenzhen,Qingdao.

Q: What is payment terms?

A: T/T,L/C, West Union.

Q: What information should I offer to you if I want to know the price?

A: Appication/usage,Size,Material,Quantity,Package term,Delievery time,Payment term,Destination.

Q: What is your warranty?

A: By National Standard GBT 10504-2008, Offer lifetime consultation on problems occurred.

FAQ

Why choose products from KANGYU ?

1. Specialize in this field for more than 10 years.

2. More than 1000 workers, Strong ability of production.

3. Shorter delivery time.

4. Rich variety of products:molecular sieve,random and structured chemical packing in ceramic,plastic&metal honeycomb ceramics,inert ceramic balls,activated alumina,alumina grinding balls,expanded perlite,porous ceramic filter pipe and so on.

5. Competitive price,modern appearance.

6. Do any sticker you need(OEM,ODM).

7. Going green and environmental protection:No mercury, No radition, No UV.

8. Honesty is the most important