Zamak ingot, Zn ingot
Min. Order: 1metric ton
Supply ability: 4000 metric ton
Shape: Ingots about 12 kg
Zinc ingot, Zamak ingot

Zinc alloy "zamak 5" turkish origin according to the European origin EN1774 for the egyption market and international markets
Analysis:
Al%: 3.8-4.2%
Mg%: 0.035-0.06%
Cu%: 0.7-1.1%
Fe%: 0.02% max
Pb%: 0.003% max
Sn%: 0.001% max
Ni% 0.001% max
Cd%: 0.003% max
Zamak 5 propertiesPropertyMetric valueEnglish valueMechanical propertiesPhysical properties
USAGE:

1. Mainly used for die-casting alloy battery industry
2. Widely used in Painting/ Printing/Dyeing/pharmaceutical/rubber industry etc.
3. Chemical industries, zinc and other metal alloy plating coating industry
4. In zinc plating, manufacture of brass, maganese bronze, galvanized iron, dry battery; As catalyst and reducing agent.

ltimate tensile strength	331 MPa (270 MPa aged)	48,000 psi (39,000 psi aged)
Yield strength (0.2% offset)	295 MPa	43,000 psi
Impact strength	52 J (56 J aged)	38 ft-lbf (41 ft-lbf aged)
Elongation at F max	2%
Elongation at fracture	3.6% (13% aged)
Shear strength	262 MPa	38,000 psi
Compressive yield strength	600 MPa	87,000 psi
Fatigue strength (reverse bending 5x10 8 cycles)	57 MPa	8,300 psi
Hardness	114 Brinell
Modulus of elasticity	96 GPa	14,000,000 psi
Solidification range (melting range)	380386 °C	716727 °F
Density	6.7 kg/dm 3	0.24 lb/in 3
Coefficient of thermal expansion	27.4 μm/m-°C	15.2 μin/in-°F
Thermal conductivity	109 W/mK	756 BTU-in/hr-ft 2 -°F
Electrical resistivity	6.54 μΩ-cm at 20 °C	2.57 μΩ-in at 68 °F
Latent heat (heat of fusion)	110 J/g	4.7x10 -5 BTU/lb
Specific heat capacity	419 J/kg-°C	0.100 BTU/lb-°F
Coefficient of friction	0.08

Zinc ingot
mark	chemical comporsition(%)
	Zn≥	impurity content≤
	Zn≥	Pb	Cd	Fe	Cu	Sn	Al	As	Sb	total
Zn99.995	99.995	0.003	0.002	0.001	0.001	0.001				0.005
Zn99.99	99.99	0.005	0.003	0.003	0.002	0.001				0.01
Zn99.95	99.95	0.02	0.02	0.01	0.002	0.001				0.02
Zn99.5	99.5	0.3	0.07	0.04	0.002	0.002	0.01	0.005	0.01	0.5
Zn98.7	98.7	1	0.2	0.05	0.005	0.002	0.01	0.01	0.02	1.3