No.

Property 

Unit

Test

Data

1

Melt Flow Index

g/10min

GB/T3682-2000

≤2.0

2

Density

g/cm3

GB/T1033.1-2008

≤0.955-0.978

3

Tensile strength 

Mpa

GB/T1040.3-2006

≥20.0

4

Tensile yied strength 

Mpa

GB/T1040.3-2006

≥16

5

Elongation at break

%

GB/T1040.3-2006

≥650

6

Brittle temperature at low temperature

°C

GB/T5470-2008

≤-76

7

ESCR ,FO

H

GB/T2951.41-2008

≥500

8

Oxidation induction period at 200°C

Min

GB/T2951.42-2008

≥30

9

Content of Carbon black

%

GB/T2951.41-2008

2.60±0.25

10

Carbon Black dispersion

--

GB/T18251-2000

≤3

11

Ceka softening point

°C

GB/T1633-2000

110

12

Tensile strength after thermal aging 

Mpa

GB/T2951.12-2008

≥20.0

12

Elongation after thermal aging

%

GB/T2951.12-2008

≥650

13

Elongation at Low Temperature

%

GB/T2951.14-2008

≥175

16

Dielectric strength

Mv/m

GB/T1408.1-2006

≥25

17

Volume resistivity

Ω.m

GB/T1410-2006

≥1*1014

18

Dielectric Constant ε

F/m

GB/T1409-2006

≤2.75

19

Dielectric loss factor tgδ

--

GB/T1409-2006

≤0.005