Granulated Blast Furnace Slag Granulated Blast Furnace Slag
USD $45 - $60 /Forty-Foot Container
Min.Order:1 Forty-Foot Container
We are on the leading names engaged in by PhraseFinder">trading of fine quality blast furnace iron slag. Quenching of molten iron slag (a iron and steel manufacturing by-product) using water or steam in a blast furnace produces blast furnace slag.
GROUND GRANULATED BLAST FURNACE SLAG/GGBFS S95
High refractoriness
High combine intensity
Stable chemical by PhraseFinder"> properties
1. Product Description:
The Ground Granulated Blast Furnace Slag (GGBS) is a type of eco-friendly green building material and high quality secondary cementitious material for concrete and cement. It is recognized as one of the best secondary cementitious material for building high durable concrete strecture in the world by PhraseFinder"> today !GGBS has taken over by PhraseFinder"> top place of high-performance cement and concrete mineral additives with its unique characteristics of hydration,low-price raw material.
GGBS is obtained by quenching molten iron blastfurnace slag (a by- product of iron and steel making) in water or steam. It is then further grounded into the desired fineness in terms of the required particle size distributionm.
2. by PhraseFinder"> Applications & by PhraseFinder"> Benefits For the product:
Ⅰ. High-performance concrete additive, especially suitable for:
A. Preparation of the harbor and marine concrete structures with high resistance to corrosion by chloride ion.
B. Preparation of corrosion resistant concrete, improving durability of concrete structure in soleplate salt and alkali regions.
C. Preparation of concrete which provides by PhraseFinder"> effective prevention measures for the potential by PhraseFinder"> active alkali-aggregate reactions in concrete.
D. Preparation of low heat concrete which, effectively reducing the risk of temperature cracks in early period of the mass concrete structure.
E. Preparation of pumping concrete to effectively reduce the slump loss in the construction in summer, hence improving the workability of concrete.
F. Preparation of self compacting concrete to have effective control on bleeding and segregation of high fluidity concrete.
Ⅱ, Super-reactive cementitious additives, especially suitable for:
A. Production of medium content (30-50%) slag cement, improving the strength of all ages.
B. Production of low heat cement with high GGBS substitutions (50-70%), used for mass or port/marine concrete structures.
Property Result Test Method
Fineness blaine 419 GB/T 8074-2008
loss on ignition 0.68 GB/T 176-2008
Sulfide slfur (S) 1.083 GB/T 176-2008
Sulfuric anhydride(SO3) 0.36 GB/T 176-2008
Magnesium oxide(MgO) 11.3 GB/T 176-2008
Alumina(AL2O3) 14.5 GB/T 176-2008
Total iron(FeO) 0.8 GB/T 176-2008
Manganese(MnO) 0.57 GB/T 176-2008
Chloride(CL) 0.012 GB/T 176-2008
Insoluble residue 0.23 GB/T 176-2008
Mortar compressive at 03 days 16.50 GB/T 18046-2008
strength(Mpa) at 07 days 32 GB/T 18046-2008
at 28 days 55 GB/T 18046-2008
at 03 days 55 GB/T 18046-2008
by PhraseFinder"> Activityindex(%) at 07 days 80 GB/T 18046-2008
at 28 days 98 GB/T 18046-2008
Standard
GB/T 18046(Chinese standard)
BS EN 15167-1 BS 6699 (UK standard)
Packing
1.5MT Jumbo Bag OR bulk ship in vessel in a enough quantity or as your requirements