Specifications

EVA cup mat/eva form mat/eva foam cup mat
1)hardness: 20-90 shores
2)SGS approval

EVA cup mat/eva form mat/eva foam cup mat

 

1.material:EVA 
2.any size
3.thickness:According to your requirement.

4.hardness :20-90 shores
lor:any color is available

6.Prinitng are accepted.

7.Good quality and environmental protection.

8.Application:Widely used in garden kneeling

9.package:poly bag

10.Terms of payment: L/C ,T/T

11.Delivery time :20 days

12.Packing;Poly bag /Export carton,our factory can also pack according to customers demand.

 

EVA foam is closed cell foam made from Ethylene Vinyl Acetate and blended copolymers. It has a high level of chemical cross linking. The result is semi-rigid product with a fine uniform cell structure that is suitable for use in

a wide variety of situations and applications. Benefits of EVA Foam include;

• Impact and vibration absorption
• Weather and chemical resistance including splash resistance to oils and fuels
• Acoustic and thermal insulation properties
• Buoyancy with low water absorption
• Suitability for thermo-forming and thermo-moulding

EVA sheet is featured by its elasticity, duration, light weight, skid and water proof, easy to wash, and widely used in professional competition gyms mats, training gyms mats, school pool mats, school and amusement grounds mats. Its well accepted by the customers both at home and abroad because of its low price and good quality.
Mylon is an experienced EVA foam producer. More than 10 years ago, we are purely an EVA foam material supplier for EVA closed cell dense foam. Our EVA foam supplied the shoes industry and other related businesses. Until now, we still arrange 40% to 50% of our production for the EVA foam product's manufacturers / processors.
Mylon- At a glance
Currently, we supply the manufacturers of Carpet, double-sided adhesive tape, shoes, arts and crafts, stationery, message boards, foam toys, sporting goods and others
Water resistance: Airtight bubble pore structure, non-absorbent, moisture-proof and waterproof properties is good.Corrosion resistance, oil resistance, water, acid and alkali corrosion, such chemicals antibacterial, non-toxic, tasteless, no pollution.

 

Application:
Household appliances, hardware tools, toys, crafts, tourism products, stationery, cosmetics,
The skates, shoes, sports lining materials back cushion, bags, mat mat; The knees surfboard,
Sports equipment, automobile interior trim, shoes joint,

 

Item No.	L-2500	C-1600	C-3000	H-25	H-35	A-25
Density (g/cm^3)	0.021~0.027	0.035~0.041	0.023~0.029	0.065~0.075	0.07~0.08	0.08~0.09
Hardness (type C)	15~21	24~30	7~13	25~30	30~35	25~30
Original Sheet Size (cm)	100*200	100*200	100*200	100*200	100*200	100*200
Original Sheet Thickness (mm)	80	80	80	36	32	38
Tensile Strength (kg/cm^2)	2.0	3.2	2.8	9.5	11.8	9.5
Elongation at Break (%)	180	180	340	220	160	120
Tear Strength (kg/cm)	1.9	2.4	2.1	3.4	3.8	3.3
Compressive Strength at 25% Deflection (kg/cm^2)	0.4	0.6	0.3	0.7	0.8	0.7
Compressive Strength at 50% Deflection (kg/cm^2)	1.0	1.3	0.8	1.5	1.8	1.6
Compression Set to 50% of Original Thickness (%)	10	14	17	20	20	20
Water Absorption (%, by weight, room temp., 5 hrs)	< 1	< 1	< 1	< 1	< 1	< 1
Type	PE/EVA	PE/EVA	EVA/PE	EVA/PE	EVA/PE	EVA

  

Item No.	A-35	RE-1050	B-20HV	P-560	P-565
Density (g/cm^3)	0.075~0.085	0.075~0.085	0.11~0.115	0.125~0.135	0.17~0.18
Hardness (type C)	32~38	45~50	20~25	55~60	60~65
Original Sheet Size (cm)	100*200	94*188 100*200	100*200	90*180 110*235	100*190 100*220
Original Sheet Thickness (mm)	24	32 40	43	32 32	28 28
Tensile Strength (kg/cm^2)	9.4	13.0	9.3	18.8	26.4
Elongation at Break (%)	90	130	140	120	150
Tear Strength (kg/cm)	3.2	3.3	2.8	5.6	8.3
Compressive Strength at 25% Deflection (kg/cm^2)	0.8	0.9	0.5	0.8	1.4
Compressive Strength at 50% Deflection (kg/cm^2)	1.5	1.5	1.2	1.3	2.4
Compression Set to 50% of Original Thickness (%)	10	30	20	2	1
Water Absorption (%, by weight, room temp., 5 hrs)	< 1	< 1	< 1	< 1	< 1
Type	PE/EVA	PE/EVA	EVA	EVA/PE	EVA/PE

  

spec: 1m*1m
examination project		unit	name
			L-1500	L-2000	L-2500	L-3000	L-4000
tensile strength at break		mpa				0.25-0.3
elongation at break		%	240-290	220-250	180-230	170-200	150-180
ASKER“ C” hardness		°	40-45°	30-35°	20-25°	15-20°	12-15°
tear strength		KN/M			7-10	8.5-11	9-12
density		Kg/m 3	60Kg/m 3	50Kg/m 3	40Kg/m 3	30Kg/m 3	25Kg/m 3
compression set		%				54.2
compression set	Ø 23mm        specimen	%	0.2 percent of pass94%	0.2 percent of pass94%	0.2 percent of pass94%	0.2 percent of pass94%	0.2 percent of pass94%
24h*25%	50*50mm  specimen	%
combustion test(straight)		B1			32	32	32
		B2			26	26	26
		ignitability				≤ 150