Description

Materials

Tolerance

Range

HMR

Milliohm Resistors

Nicke&copper alloy wire

Manganin wire

±1%,±5%,±10%

1mR-100mR

JWR/CJW

Jump Wire Resistors

Copper wire, CP wire

±5%

0R

Test Item

Test Condition

Performance

Temperature coefficient

Test the resistance value at normal temperature and normal temperature added 100℃,calculate per℃ resistance value change rate .

±5~50ppm/℃

Resistance to soldering heat

Immerge into 350±10℃ tin stove for 2~3 seconds.

ΔR≤±(0.5%R0+0.05Ω)

Solderability

Immerge into 245±3℃ tin stove for 2~3 seconds.

The area of soldering is over 95%

Temperature cycling

At  -55℃ for 30 min, then at +25℃ for 10~15 min, then at +125℃ for 30 min, then at +25℃ for 10~15 min, total 5 cycles.

ΔR≤±(0.5%R0+0.05Ω)

Load life in humidity

Overload rated voltage or ing voltage (get the lower) for 1000 hours (1.5 hours on and half-hour off ) at the 40±2℃ and 90~95% relative humidity.

ΔR≤±(2%R0+0.05Ω)

Load life in heat

Overload rated voltage or ing voltage (get the lower ) for 1000 hours (1.5 hours on and half-hour off) at the 70±2℃. 

ΔR≤±(2%R0+0.05Ω)

HMR

CN

045

B34

J

0R005

Product Name

Materials

Dia.

Forming

Tol.

Ohm

Milliohm Resistors

CM:Manganin

NC:Nickel chrome

TG:Iron chrome

BX:Flat wire

MT:Tinned CM

NT:Tinned NC

TT:Tinned TG

CN:Copper&nickel alloy

045=0.45

100=1.00

(uint=mm)

B34:

Axial of 34mm

F=±1%

J=±5%

K=±10%

0R005=5mΩ

0R010=10mΩ

0R100=100mΩ