magnetron sputtering machine for solar glass tube coating machine
USD $35,000 - $100,000 /Set
Min.Order:1 Set
Hongfeng Mechanical Equipment Manufactory
Vacuum Plating Plant and Equipment for Metal/ceramic tile plasma coating equipment
Magnetron Sputtering and Multi Arc System/bracelet decorative pvd coating machine
Vacuum Magnetron Sputtering and Multi Arc Ion Coating Equipment and System
PVD Vacuum Sputtering and Multi Arc Ion Plating Equipment and System
magnetron sputtering machine for solar glass tube coating machine
A series of metal-aluminium nitride (M-AlN) cermet materials for solar selective coatings was deposited by a novel direct current (d.c.) magnetron sputtering technology. Aluminium nitride was used as the ceramic component in the cermets, and stainless steel (SS), nickel-based alloy (NiCr), molybdenum-based alloy (TZM) and tungsten were used as the metallic components. The aluminium nitride ceramic and metallic components of the cermets were deposited by simultaneously running both an aluminium target and another metallic target in a gas mixture of argon and nitrogen. The ceramic component was deposited by d.c. reactive sputtering and the metallic component by d.c. non-reactive sputtering.
The total sputtering gas pressure was 0.8-1.0 Pa and the partial pressure of reactive nitrogen gas was set at 0.020-0.025 Pa which is sufficiently high to ensure that a nearly pure AlN ceramic sublayer was deposited by d.c. reactive sputtering. Because of the excellent nitriding resistance of stainless steel and the other alloys and metal, a nearly pure metallic sublayer was deposited by d.c. sputtering at this low nitrogen partial pressure.
A multilayered system, consisting of alternating metallic and AlN ceramic sublayers, was deposited by substrate rotation. This multisublayer system can be considered as a macrohomogeneous cermet layer with metal volume fraction determined by controlling the thicknesses of metallic and ceramic sublayers. Following this procedure, M-AlN cermet solar selective coatings with a double cermet layer structure were deposited.
The films of these selective surfaces have the following structure: a low metal volume fraction cermet layer is placed on a high metal volume fraction cermet layer which in turn is placed on an aluminium metal infrared reflection layer. The top surface layer consists of an aluminium nitride antireflection layer. A solar absorptance of 0.92-0.96 and a normal emittance of 0.03-0.05 at room temperature have been achieved for these M-AlN cermet solar selective coatings.