Specifications

furnace UL type electric MoSi2 heater
1.temperature:1700C,1800C
2.shapes:I,U,W,UL,WL
3.Density:5.5-5.6g/cm3

1800C lab furnace UL type electric MoSi2 heater

1. Temperature type:1700C,1800C
2. Shapes:I,U,W,UL,WL
3. Density:5.5-5.6g/cm3

4. Diameter: 3/6, 4/9, 6/12, 7/12, 9/18, 12/24mm

 

         MoSi2 heating element is a kind of resistance heating element basically made of high pure Molybdenum Disilicide. In oxidizing atmosphere, on the surface of MoSi2 element owing to the high temperature combustion a layer of compact quartz protective film is formed to prevent MoSi2 from continuously oxidizing. Therefore, molybdenum disilicide elements have unique high-temperature oxidation resistance. In oxidizing atmosphere, its Max temperature can reach 1800°C, and its applicable temperature is 500-1700°C. It can be widely used in such applications as sintering and heat treatment on ceramics, magnet, glass, metallurgy, refractory, etc.

       MoSi2 heating element’s resistance does not change with use, in other words, that is not aging, so you can mix old and new components.

 

 

 

Volume density	Bend strength	Vickers hardness	Porosity rate	Water absorption	Hot extensibility
5.5~5.6 g/cm3	15~25 kg/cm2	(HV)570 kg/mm2	7.4%	1.2%	4%

 

        Oxygen-resistance under high temperature: In oxidizing atmosphere, on the surface of element owing to the high-temperature combustion a layer of compact quartz (SiO₂) protective film is formed to prevent MoSi2 from continuously oxidizing. When the element temperature is higher than 1700°C, the SiO₂ protective film, whose fusing point is 1710°C, is fused, and the SiO₂ is fused into molten drops owing to the action of its surface extension, so that loses its protective ability. In the oxidizing atmosphere, when the element is continuously used, again the protective film forms.

      It should be pointed out that element cannot be used for rather long time in 400-700°C,otherwise it will be powdered owing to the strong oxidizing action in low temperature.

The Max temperature of elements in different atmospheres

Atmosphere	Max element temperature
	Clyde Super 1700 Type	Clyde Super 1700 Type
Air	1700°C	1800°C
Nitrogen	1600°C	1700°C
Argon, Helium	1600°C	1700°C
Hydrogen	1100~1450°C	1100~1450°C
N2/H295/5%	1250~1600°C	1250~1600°C
General Applications	Most types of industrial furnace for heat treatment, forgoing, sintering, glass smelting and refining and for use in radiant tubes	Laboratory furnaces, testing equipment and high temperature sintering

 