Grade

Enquivalent

To ISO

Density

(g/cm3)

HRA

T.R.S

(Mpa)

Application

JT6

K20

14.9

≥90.0

≥2150

High wear resistance, used for hard wood, used for processing original wood, 

aluminum section bar, brass rod and cast iron.

JT6A

K10

14.9

≥92.0

≥1850

Higher wear resistance than YG6, used for processing hard wood, 

original wood, aluminum section bar, brass rod and cast iron.

JT8

K30

14.7

≥89.5

≥2320

High wear and percusstion resistance,used for processing hard wood, 

soft wood, ferrous and non ferrous section bars.

YS2T

M30

14.5

≥91.5

≥2300

Fine grain alloy, high wear resistance, high anti-bending strength, high resistance to bonding, high thermal strength. 

Machining of refractory alloys, stainless steel and high manganese steel, etc.

YL10.2

K10

14.5

≥91.8

≥2500

Wear resistance and strength comparatively higher, suitable for processing cast iron, non-ferrous and non-metal materials.