Varistor/Surge protector, buy high voltage surge protector zinc metal oxide varistor surge arrestor surge absorber 10mm 10D471K WMR on China Suppliers Mobile

Product Details

Product Description

Type MYG Varistors are made of semiconductor ceramic materials composed mainly of zinc oxide. They have non-linear resistance that change as a function of applied voltage. It has small size, high current capacity, and high protection level.

Dimension: Dmax=12mm; Hmax=15mm;Lmin=15mm;T=9.0mm; d0.8+/-0.03; A=7.5+/-1mm;

PRODUCT:HEL10D471K

Varistor voltage(V1mA):470V/423-517V

Maximum Allowable voltage:300VAC/385VDC

Maximum Clamping voltage:775V

Withstanding Surge Current(8/20us):2500A/1 time

Rated Wattage(W):0.4W

Energy(2ms):42.3J

Typical Capacitance:190PF

Ordering Notes:

1. Ceramic Disc: Zinc Oxide Varistor

2. Material of coating: Epoxy resin

3. Material of Leads: CP wire

4. Lead type: Straight lead

5. Package: Bulk pack

1. Varistors Voltage: The voltage between two terminals with the specified measuring current 1mA DC applied is called V1mA,The measurement shall be made as fast as possible to avoid heat affection.

2.Maximum Continuous AC or DC Voltage:Maximum Continuous AC Voltage 0.62multility varistor voltage.

3. Leakage Current: The current passing through the varistors at the maximum continuous DC voltage.

4.Clamping Voltage:The peak voltage at class current (Standard surge currentwaveform is 8/20μS). The class current is a peak value of current which is1/10 of the maximum peak current for 100 impulses at per minute for 8/20μS.

5.Energy:The maximum energy within the varistors voltage change of ±10% when one impulse of 2ms or 10/1000μS is applied.

For the 2mS waveform:J=2*Ip* Vc*10-3 For the 10/1000μS waveform:

J=1391*Ip* Vc*10-6 Where J -- Energy absorbed in joules.

Ip -- Maximum let-through current in amps.Vc-- Measured clamping voltage in volts.

6.MaximumPeak current : The maximum current within the varistors voltage change of ±10% with the standard impulse current (8/20μS) applied one time.

7. Capacitance: Typical value measured at 1Vrms and test frequency of 1kHz.

8.Solderability: After dipping the terminals to a depth of 3.5-0.5 mm from the body in a soldering bath of temperature 235℃±5℃for 2± 0.5seconds, the terminal shall be visually examined.

9.Resistance to Soldering heat: After each lead shall be dipped into a solder bath having a temperature 260℃±5℃,to a point 2.0 to 2.5mm from the body of the unit. Using shielding Board(t=1.5mm) ,be held there for specified time(5D series: 5±1 seconds and other series:10 s ),and then be stored at room temperature and humidity for 1 to 2 hours. The change of V1mA and mechanical damages are examined.

10.Solvent resistanceof marking:Solvent: alcohol Rubbing material: cotton wool Recovery: 4hours.

Thereafter, visual examination and the change of V1mA shall be examined.

11.Component Solvent resistance:Solvent:70±5% and F113+30±5% strang third mellow mixture,Solvent temperature:23+5℃,5±0.5Min.Recovery: 4hours.Thereafter, visual examination and the change of V1mA shall be examined.

12. Robustness of Terminations:

After gradually applying the force specified below and keeping the unit fixed for ten seconds. The terminal shall be visually examined for any damage.

Lead diameter(mm): 0.6 0.8 1.0 Force (N): 1 10 20

13.Shock(or bump):

Pulse shape half sine acceleration:490 m/s².Pulse duration:11ms.

Thereafter, visual examination and the change of V1mA shall be examined.

14.Virbration:

Frequency range:10Hz--55Hz.Amplitude: 0.75mm or 98 m/s²whichever is the less severe.Total duration: 6 hours .Thereafter, visual examination and the change of V1mA shall be examined.

15.Temperature Cycle: Condition the specimen to each temperature from step 1 to step 4 in this order for the period shown in the table of specifications. The change of V1mA and mechanical damage shall be examined after 24±2 hours.

16.Damp Heat /Humidity(SteadyState):

The varistor shall be divided into two groups

The first group shall be subjected to this test without voltage applied, The second group shall be

Applied a DC voltage . Ambient condition.: 40℃±2℃, 90~95%RH Period: 1000 ±24hours

Then stored at room temperature and normal humidity for1 to 4hours. Thereafter, the change of V1mA and the insulation resistance shall be examined.

17.Endurance at upper category temperature:

The specimen shall be applied continuously the Max. AC allowable voltage at 1000 Hours and 85℃±2℃

The specimen shall be applied in cycles of 90Min on and 30Min off throughout the test .

Then stored at room temperature and normal humidity for 4±0.5 hours. Thereafter, the change of V1mA and the voltage at class current ,the insulation resistance and mechanical damage shall be examined.

18.Climatic Category:

Dry heat:+85℃±2℃,16hours;Damp heat,cyclic:IEC68-2-30 Test Db, 55℃,First cycle 24 hours;Cold:-40℃±3℃,2 hours;(Low air pressure test not applicable)Damp heat,cyclic, Test Db, remaining cycles.Then stored at room temperature and normal humidity for 1 to 2 hours. Thereafter, the change of V1mA and the insulation resistance shall be examined.

Packaging & Shipping

Packing:1000pcs/plastic bag

Shipping: FOB,EXW,CNF. Please notify me if you have any special needs.

Our Services

We can provide you the best professional technical support, such as data sheet, drawing, design FAQ, ect,.

We also can provide you the related recognize credit, such as UL,VDE,CSA,CQC,ect.