EMBOSSING COATING (L-TYPE)

TYPE

Two-pack, based on Saturated fatty acid resin and Polyisocyanate Hardener with special pigments.

USES

Top coat for steel structure for machine and , office furniture,. Medical Equipment

CHARACTERISTICS

1. Excellent appearance.

2. Excellent hardness, adhesion and abrasion resistance.

APPLICATION METHOD

Airless Spray, Roller, Brush.

COLOR

Desired colors

FINISH

50 %

SPECIFIC GRAVITY

Above 1 kg/L (Mixture)

VISCOSITY (25℃)

55 ~70 KU (Mixture)

DRYING TIME (25℃)

Set-to-touch

Dry hard

2 hr.

8 hrs.

FILM THICKNESS

Wet

Dry

70 ~100 microns

30 ~50 microns

SOLIDS (by Weight)

Above 50%

THINNER

PU Thinner

THINNING RATE

10 ~25 %(by wt.)

PRECEDING COATS

Red Oxide Primer or Epoxy Primer

STORAGE SHELF LIFE

Minimum 1 year under normal storage conditions.

MIXING RATIO

Base: Hardener = 3 : 1 (by volume.)

POT LIFE

4 hrs. (Mixture) (25℃)

NOTE

1. Mix base and hardener according to the mixing ratio and stir

    thoroughly.

2. Moisture, grease, rust, dirt and loose paints film on substrate must be

    removed, so are the corrosive salt particles. As a result, paint

    performance can be ensured.

3. Hardener must be tightly closed to avoid reaction with moisture in air

    toform bubbles and gelation.

4. Attention to the pot life.

5. Strictly controlling application, not to exceed 50 μ per coat, to avoid

    bubble formation.

6. All equipment must be cleaned immediately after use.

7.Avoid applying the paint in rainy weather or humidity above 85% RH,

   particularly, a wet surface must be thoroughly dried