Specifications

1.High hardness;
2.Even hardness and long life;
3.High wear-resistance;
4.High impact toughness:
5.Unbreakable

Features:

 

Best selling steel products--JINCHI hot-forging (hot-rolling) alloy steel grinding mill ball :
1.High hardness;

2.Even hardness no matter surface or core;

3.High wear resistance,more dense tissue and abrasion lower;

4.High impact toughness ;
5.Unbreakable;

6.No deformation;

7.Good apperance and look better;

8.Long life;

9. High combined efficiency of grinding mill;
10.Manufacturerer

 

JINCHI Forging (Rolling) Steel Grinding Ball Advantage:

 

1.Professional manufacturer for alloy steel grinding ball;

2.Easy Storage;

3.Accept customized order;

4.Fast delivery;

5.Regional manager track;

6.After -sale service;

7.Emergency supply;

8.Factory price and Best quality;

9.Offer the solutions to your problems,we promise all your inquiries and messages will get our reply within 12 hours;

10.SGS Service

 

Specifications and Hardness of Forging Ball:

 

Nominal  Diameter (mm)	Diameterical  Tolerance (mm)	Weight of Single  Forging Ball in  Average(g)	Number of piece  of OneTon Forging  Ball in Average	Surface  Hardness (HRC)	Impact  Toughness (j/cm2)
¢20 ¢ 25 ¢ 30 ¢ 40 ¢ 50	+2 -1	32 64 110 263 513	31250 15625 9090 3802 1949	50-65	≥12
¢ 60 ¢ 70 ¢ 80 ¢ 90 ¢ 100	+3 -2	888 1410 2104 2996 4110	1126 709 475 333 243
¢ 110 ¢ 120 ¢ 130	+4 -2	5457 7102 9030	182 140 110	45-60
¢ 140 ¢ 150	+4 -3	11278 13871	88 72

 

Physical Property of Forged Alloy Steel Ball:

 

Materials	Impact Test (Ak.J/cm²)	Endurance Test Times (5m/T)	Surface  Hardness (Dia25mm-90mm)	Core  Hardness (Dia25mm-90mm)	Surface  Hardness (Dia90mm-150mm)	Core  Hardness (Dia90mm-150mm)	Breakage
50Mn	≥12	≥10000	≥52	≥42	≥50	≥40	<0.5%
60Mn	≥13	≥10000	≥52	≥42	≥50	≥40	<0.5%
65Mn	≥15	≥12000	≥54	≥44	≥52	≥42	<0.5%
B2	≥17	≥12000	≥60	≥52	≥58	≥50	<0.5%
75SiMn	≥16	≥12000	≥60	≥52	≥58	≥50	<0.5%
Impact -resistant Alloy	≥17	≥10000	≥50	≥40	≥48	≥38	<0.5%
Wear-resistant Alloy	≥17	≥12000	≥60	≥52	≥58	≥50	<0.5%

 

 

 

The Chemical Composition of Forged Alloy Steel Ball Is as Follows:

Material	C	Si	Mn	Cr	S	P	Times of Endurance impact test
50Mn	0.48-0.56	0.17-0.37	0.70-1.00	≤0.25	≤0.035	≤0.035	≥10000
60Mn	0.57-0.65	0.17-0.37	0.70-1.00	≤0.25	≤0.035	≤0.035	≥10000
65Mn	0.62-0.70	0.17-0.37	0.90-1.20	≤0.25	≤0.035	≤0.035	≥12000
B2	0.65-0.78	0.17-0.37	0.70-1.20	0.55-0.60	≤0.035	≤0.035	≥12000
75SiMn	0.70-0.90	0.40-0.80	0.70-1.20	≤0.25	≤0.035	≤0.035	≥12000
Impact -resistant Alloy	0.37-0.45	0.20-0.45	0.50-1.00	0.80-1.20	≤0.035	≤0.035	≥10000
Wear-resistant Alloy	0.75-0.90	0.15-0.42	0.65-1.10	0.88-1.20	≤0.035	≤0.035	≥12000

 

The Process Lline of Production:

 

FAQ:

 

1.Q: Can you tell me the key factors which can decide the quality of the grinding balls?
   A: They are the raw material, the strict process control,the hardness, the impact toughness, especially the raw material and the heat treatment.

2.Q:Can I see the difference just from the surface of the balls?
   A: In general, you can not see the obvious difference from the surface of the balls. 

3.Q: How can I make sure you are a reputable supplier? 
   A: Actually, there is no need to have any doubts about our reputation.High quality products,high

quality service and own research development manufacturing make our reputation.

 

         We believe that corporate reputation is the most important principle for a company to exist.

 

Ours' Certificate: