Two Component Polyurethane Adhesive Application

Wood composite panels:PU201

² Properties: room temperature vulcanized; formaldehyde free ;moderate viscosity easy for operation;               good water and thermal resistance;  good warpage and mildew resistance

² Application: woods(except mahogany)

² Technical data (at 25℃)

• Ø Viscosity: A:10000cps; B:220cps
• Ø Mixing ratio (weight):100/25
• Ø Press time:2-3 hours   

² Can use mix equipment and coating machines to improve production efficiency.

Floors, runways, playgrounds:PU202

² Properties: sag resistance; excellent bond strength ; thermal resistance; good thixotropy.

² Application: wooden floors, tiles, metal plates, plastic plates.

² Technical data (at 25℃)

• Ø Viscosity: A:pasty; B:220cps
• Ø Mixing ratio (weight):100/25
• Ø Press time:3 hours   

² It can be used in places that require sag resistance, such as inclined, vertical and overhead.

Cellular plates(walls, TV towers, high-speed trains and gyms):PU203

² Properties: moderate viscosity; excellent bond strength; good fire and thermal resistance .

² Application:cellular plates, metal plates, wood, glass, fiberglass panels, glass magnesium boards, etc.

² Technical data (at 25℃)

• Ø Viscosity: A:28000cps; B:220cps
• Ø Mixing ratio (weight):100/25
• Ø Press time:2-3 hours   

² It can be used to assemble flame-resistant materials.

Insulation boards(foam boards,rock wool board):PU204

² Properties:good liquidity;50-100% foaming rate; excellent bond strength; thermal resistance .

² Application:metal boards, foam boards and melamine boards, etc.

² Technical data (at 25℃)

• Ø Viscosity: A:11000cps; B:220cps
• Ø Mixing ratio (weight):100/30
• Ø Press time:3 hours   

² It can be used to assemble sandwich panels or security doors.

Fire doors:PU205

² Properties: moderate viscosity; excellent bond strength; thermal resistance.

² Application:metal plates, wood, tiles, fiberglass panels, glass magnesium boards, foam boards,

       rock wool boards, etc.

² Technical data (at 25℃)

• Ø Viscosity: A:15000cps; B:220cps
• Ø Mixing ratio (weight):100/20-25
• Ø Press time:2-3 hours   

² It can fast cure in room temperature.