Modified Epoxy Nonferrous Metal Primers
USD $4.35 - $4.85 /Metric Ton
Min.Order:1 Metric Ton
Chongqing Hi-Sea Marine Equipment Import & Export Co., Ltd.
Modified Epoxy Nonferrous Metal Primers :
FXH02-7 Modified Epoxy Nonferrous Metal Primers
Characteristics: Excellent adhesion with zinc material,aluminum material,stainless steel etc. nonferrous metal.
Uses: Mainly use for zincification material,aluminum material, copper material etc. nonferrous metal substrate, as a use of linking paints.
Technical target:
Mixing ratio: Host crystal/Firming agent=8/1(by weight)
Standard film thickness: Dry: 30μm/coat
Academic spreading rate: 0.09kg/ m2/30μm
Solid contents: 71.3%
Humidity requirement: below 85%
Drying time & Coating interval
Temperature °C | -10 | 0 | 10 | 20 | 30 |
Dry to touch (hrs) | 4 | 2.5 | 2 | 1.5 | 1 |
Dry semi-hard (hrs) | 36 | 24 | 14 | 10 | 8 |
Min. interval (hrs) | 36 | 24 | 14 | 10 | 8 |
Substrate treatment;Remove surface oil stain,dust and zinc salt of the zinc material etc. nonferrous metal.
Matching:
Applicable substrate: Zinc material,aluminum material,stainless steel etc. nonferrous metal.
Applicable upper coatings: Compatible with all intermediate paints,finishes