Specifications

balster cleaning using single inlet abrasive nozzle
1) b4c blasting nozzles
2) single venturi nozzle

balster cleaning using single inlet abrasive nozzle

b4c sandblasting single venturi nozzles for outdoors sandblaster

 

Characteristic:

The inner core use imported high purity boron carbide raw materials, produce with high-tech equipment and fine process.Nozzle have long service life, high hardness, high strength, high chemical stability, light weight, high temperature resistance, corrosion resistance and other characteristics,which is 3-4 times service life than tungsten carbide nozzle.

We also have higher performance upgrades for most OEM products to allow you to achieve optimum blasting effectiveness, efficiency and reduce your total costs.

 

Approximate Nozzle Service Life in Hours 

 

Nozzle material       Steel Shot and Grit    Expendable Abrasives    Alu-oxide Abrasives
Ceramic                                20 - 40                      10 - 30                                  1-4
Tungsten Carbide                500 - 800               300 - 400                            20-40
Silicon Carbide / Nitride   600 - 1000               400 - 600                           50-100
Boron Carbide                 1500 - 2500                 750 - 1500                      200 – 1000

 

* Estimated values for comparison. Actual service life will vary depending upon 
blast pressure, media size and particle shape.

 

 Hardness:HRA92-94

Density:4.50-4.60g/cm3

Bending strength:40kg/cm2

Compression strength:240kg/cm2

Appearance: carbon steel shell after sand blasting and plating, aluminum shell after sand blasting.

Model	Bore  diameter	Length	Inner core	Shell material	Remark
S001	6mm	162mm	boron carbide	carbon steel	Aluminum shell can be customized
S002	8mm	162mm	boron carbide	carbon steel
S003	10mm	162mm	boron carbide	carbon steel
S004	12mm	162mm	boron carbide	carbon steel

Notes: Nozzles can be custermized as per your request 

              Thread options: coarse thread / fine thread

 

If you want to know more information, please contact with me.Thanks!

 

Production process:

 

1.Boron carbide and other raw materials grind in ball crusher(72 hours) 

2.die-filling

3.hot press molding(2500°C)

4.natural cooling

5.Mould unloading

6.end preparation

7.Shell processing and surface treatment

8.Assemble

9.Inspection and storage

 

The different between single venturi and double venturi nozzle:

 

Single venturi nozzle is the long-range type, one air inlet. Double venturi belongs to high speed type, with eight holes around the shell, due to the high speed air flow, the speed of air ejecting faster than compressed air, speed of blasting is higher. 

 

 

1) coarse thread single venturi nozzle:

 

2) fine thread single venturi nozzle:

 

 

3) Suggesting additional purchase (Holder for nozzles):