Test Item

Ordinary Model

J-70

JR-70

H-70

HR-70

HⅡ-90

J-80

J-105

H-105

J-90

Density g/cm³

1.43

1.45

1.42

1.40

1.42

1.42

1.45

1.42

1.43

Tensile Strength/MPa

18.0

17.5

17.5

17.0

19.0

19.0

20.0

19.0

20.0

Elongation at Break /%

300

310

320

340

300

300

280

300

280

Thermal Deformation/%

33

35

38

42

30

25

25

30

25

Variation on Tensile Strength after Aging%

-5

-5

+3

+5

+5

+5

+2

+5

+5

Variation on Elongation at Break after Aging %

-8

-8

-10

-12

-12

-10

-10

-10

-12

Loss Of Mass g/m2

15

15

20

22

15

15

12

17

15

Impact Brittleness Temperature /℃

-17

-21

-25

-30

-21

-17

-16

-21

-17

Thermal Stability Time at 200℃(min)

80

80

80

80

200

100

120

200

200

Volume Resistivity at 20℃(Ω·m)

2.0×10¹²

3.0×10¹¹

4.0×10¹⁰

2.0×10¹⁰

4.0×10¹⁰

3.0×10¹²

3.0×10¹²

4.0×10¹⁰

3.0×10¹²

Dielectric Strength(MV/m)

25

24

24

24

24

25

25

25

25

Volume Resistivity at Operating Temperature(Ω·m)

3.0×10⁹

5.0×10⁸

/

/

/

5.0×10⁹

8.0×10⁸

/

8.0×10⁸

Dielectric Strength(MV/m)

25

24

24

24

24

25

25

25

25

Test Item

Eco-friendly Model

J-70

H-70

Density g/cm³

1.45

1.45

Tensile Strength/MPa

20.0

18.0

Elongation at Break /%

300

300

Thermal Deformation/%

Variation on Tensile Strength after Aging%

0

+5

Variation on Elongation at Break after Aging %

-5

-5

Loss Of Mass g/m2

12

15

Impact Brittleness Temperature /℃

-17

-22

Thermal Stability Time at 200℃(min)

80

100

Volume Resistivity at 20℃(Ω·m)

2.0×10¹⁰

8.0×10⁹

Dielectric Strength(MV/m)

25

24

Volume Resistivity at Operating Temperature(Ω·m)

/

/

Environmental Performance

Comply with RoHS 6 requirements

Comply with RoHS  6 requirements