Low ash Low sulpur carbon electrode paste
Negotiable /Metric Ton
Min.Order:1 Metric Ton
Lianyungang Jinli Carbon Co., Ltd.
Carbon Electrode Paste/Carbon Paste/Electrode Paste
Application:
Carbon Electrode Paste is a self-baking electrode used in submerged arc furnaces for delivering power to the charge mix. Electrode Paste is added to the top of the electrode column in either cylindrical or briquette form. As the paste moves down the electrode column the temperature increase causes the paste to melt and subsequently bake forming a block of electrically conductive carbon.
Specification as following:
Type 1:
Ash 2%max
Vol 11.0-14.0%
Compress Strength 20Mpa Min
Specific Resistance 65μΩm Max
Bulk Density 1.38g/cm3 Min
Plasticity 15-40%
Type 2:
Ash 3%max
Vol 11.0-14.0%
Compress Strength 20Mpa Min
Specific Resistance 65μΩm Max
Bulk Density 1.38g/cm3 Min
Plasticity 15-40%
Type 3:
Ash 4%max
Vol 11.0-14.0%
Compress Strength 20Mpa Min
Specific Resistance 70μΩm Max
Bulk Density 1.38g/cm3 Min
Plasticity 15-40%
Type 4:
Ash 5%max
Vol 12.0-15.0%
Compress Strength 17Mpa Min
Specific Resistance 68μΩm Max
Bulk Density 1.38g/cm3 Min
Plasticity 15-40%
Type5:
Ash 6%max
Vol 12.0-15.5%
Compress Strength 15.7Mpa Min
Specific Resistance 75μΩm Max
Bulk Density 1.38g/cm3 Min
Plasticity 15-40%
Type6:
Ash 7%max
Vol 9.5-13.5%
Compress Strength 19.6Mpa Min
Specific Resistance 80μΩm Max
Bulk Density 1.38g/cm3 Min
Plasticity 15-40%
Type7:
Ash 9%max
Vol 11.5-15.5%
Compress Strength 19.6Mpa Min
Specific Resistance 90μΩm Max
Bulk Density 1.38g/cm3 Min
Plasticity 15-40%
Type8:
Ash 11%max
Vol 11.5-15.5%
Compress Strength 19.6Mpa Min
Specific Resistance 90μΩm Max
Bulk Density 1.38g/cm3 Min
Plasticity 15-40%