China manufacture nickel alloy pipe incoloy 800H ASTM B407
USD $17 - $17 /Kilogram
Min.Order:300 Kilograms
Shanghai Hengtie Steel Trading Co., Ltd.
Super alloy VLX800H is a slightly modified version of Incoloy 800 with the 800H grade possessing higher creep and rupture strength. This modification is possible because of the closely controlled carbon content and modified heat treatment.
The following sections will discuss in detail about super alloy VLX800H.
The chemical composition of super alloy VLX800H is outlined in the following table.
Element | Content (%) |
---|---|
Nickel, Ni | 30 - 35 |
Chromium, Cr | 19 - 23 |
Manganese, Mn | 1.5 max |
Silicon, Si | 1 max |
Copper, Cu | 0.75 max |
Aluminum, Al | 0.15 - 0.6 |
Titanium, Ti | 0.15 - 0.6 |
Carbon, C | 0.05 - 0.1 |
Sulfur, S | 0.015 max |
Iron, Fe | Remainder |
The physical properties of super alloy VLX800H are tabulated below.
Properties | Metric | Imperial |
---|---|---|
Density | 7.9 g/cm3 | 0.287 lb/in3 |
Melting point | 1371°C | 2500°F |
Equivalent materials to super alloy VLX800H are provided below:
Super alloy VLX800H can be machined using the common processes applied to iron based alloys. This alloy does work-harden during machining and displays higher strength and "gumminess" unlike steels. It is recommended that heavy duty machining equipment and tooling should be used to reduce chatter or work-hardening of the alloy.
Any commercial coolants can be used during the machining operations; however water-based coolants are recommended for high-speed operations such as milling, turning, or grinding. Similarly, heavy lubricants are ideal for tapping, broaching, drilling, or boring.
Super alloy VLX800H can be formed using any of the conventional methods as it is very ductile. Powerful equipment is required to perform forming operations as this alloy is strong. It is recommended that heavy-duty lubricants be used while performing cold forming. It is important to clean all traces of lubricant after forming.
Welding of super alloy VLX800H can be performed using all the traditional welding methods. Matching alloy filler metal should be used. In case that is not available, it is advised that the nearest alloy closest to the chemical composition be used. The weld beads should be slightly convex, and preheating is not required. Surfaces to be welded have to be clean and free from oil, paint or crayon marking.
Forging should be performed in the temperature range of 1204-982°C (2200-1800°F).
Hot working can be performed in the temperature range of 1204-871°C (2200-1600°F).
Super alloy VLX800H can be cold formed using all the standard tools except for plain carbon tool steels as they produce galling.
Super alloy VLX800H can be annealed at 1176°C (2150°F) and then air cooled.
Super alloy VLX800H is used in the following application areas:
PackagingDetails: | Products are well packed and clear labeled according to the regulations and customer's requests. |
Delivery Detail: | 7-15days after receiving deposit |
1.Our Service For You
Pre-sale Service
1. Sample can be offered with sample charge and courier fee by buyer's side.
2. We have full stock,and can deliver within short time.Many styles for your choices.
3. OEM and ODM order are accepted, Any kind of logo printing or design are available.
4. Good Quality + Factory Price + Quick Response + Reliable Service, is what we are trying best to offer you
5. All of our products are produce by our professional workman and we have our high-work-effect foreign trade team, you can totally believe our service.
6. We have 8 year experience of design, manufacture and sell lingerie, we cherish every order from our honor.
After you choose
1. We will count cheapest shipping cost and make invoice to you at once.
2. Check quality again, then send out to you at 1-2 working day after your payment,
3. Email you the tracking no, and help to chase the parcels until it arrive you.
After-sale choose
1. We are very glad that customer give us some suggestion for price and products.
2. If any question,please contact with us freely by E-mail or Telephone.
Name:Lucy Cui
Phone:021-67896311