Name: grinding medium type Alumina Grinding ceramic pebble
Brand: Aokerola
Availability: InStock

Product Details

Specifications

grinding medium type Alumina Grinding ceramic pebble
good toughness
high density
good erosion resistance
regular shape

Application

As grinding media, this product is widely used in Ceramic industry, cement industry, paint industry, Color industry, chemical industry, pharmaceutical industry, coating industry and mining industry. The advantages are: high hardness, good toughness, high density, good erosion resistance, regular shape etc.

Technical Data

Name Items	OK70	OK80	OK90	OK93	OK95
Specific Gravity g/cm³	2.95~3.02	3.33~3.36	3.55~3.60	3.63~3.68	3.70~3.75
(Mohs Scale)Hardness	8.5	8.5	9	9	9
Compression Strength MPa	≥1700	≥1800	≥1850	≥2000	≥2250
Color	yellowish	White	White	White	White
Equivalent Wear Loss	≤0.18‰	≤0.14‰	≤0.10‰	≤0.08‰	≤0.05‰

Standard Size

Type Size Variation Size	OK70	OK80	OK90	OK93	OK95
φ30mm----φ40mm	+1.8mm	+1.8mm	+1.8mm	+1.8mm	+1.8mm
φ50mm-----φ60 mm	+2.0mm	+2.0mm	+2.0mm	+2.0mm	+2.0mm
φ70mm-----φ80mm	+3.0 mm	+3.0 mm	+3.0 mm	+3.0 mm	+3.0 mm

Remark: Other sizes are available upon requests.

Detailed Images

Company Information

AOKEROLA GROUP is the leading fine ceramic manufacturer which was established in 1990.

The main products are: high quality ceramic roller, Iso-static pressure grinding ball, wear resistant lining brick, heterotypic wear resistant ceramic, alumina packing ball, ceramic ball foundry sand, high strength prppant, active alumina ball, alumina polishin ceramic, special industry ceramic, silicon carbide ceramic and Iso-satic all press. Based on global top class hardware--a complete set of German equipment and top class software--Spanish ceramic technology, AOKEROLA manuactures over 1,500,000 pieces of quality ceramic rollers and over 100,000 tons of resistant grinding balls, lining brick and other technical ceramics and over 100,000tons of petroleum proppant and casting ceramic sands. p.a. which help us have a significant share in the world market.

History

1995	The original company of AOKEROLA GROUP, Zibo Yuanda Co. was founded.
1998	Incorporating with Spanish Refractory Institute, Weifang Aokerola Fine Cermaics Corporation was founded.
1999	Invented the isostatic medium alumina ball, and achieved the industrialization.
2000	Started the production of high alumina ball in the Weifang Plant
2001	Successfully developed the OK-Y686 iso-static ball press and won the national patent.
2002	Participated in making the National Quality Standard of Ceramic Roller in China.
2003	Successfully developed the low wear loss and low cost grinding media"Super Wear-Resistant King"
2004	Zibo Aokerola Ceramic Technology Co. Was founded.
2005	Zibo Plant started the production of medium alumina lining brick. And at the same time, Aokerola started the internationalization.
2006	Shandong Aokerola Technological Material Co., Ltd was founded, and successfully developed the global longest, full-automatic, intelligent medium alumina ball production line by high temperature roller kiln.
2007	Successfully built the unique biggest shuttle kiln for roller production, and introduced the cutting edge roller production technology from Germany inthe end of 2007.
2008	Started the production of high alumina ceramic by the High Temperature Roller Kiln, and achieved the Non-Quality-Difference production system, Which makes AOKEROLA become the first company which uses high temperature roller kiln to produce high alumina ceramic.
2010	The Fourth new high alumina ceramic production line is under construction and the Fifth new roller project is going to start.
2011	The new advanced low ware loss medium & high alumina grinding balls were brought into batch production.the medium alumina ball has been successfully replaced by the new developed high and medium alumina ball.

Images:

Exhibition Style

TECNARGILLA 2014 Rimini, Italy

Ceramic Asia 2014, India

grinding medium type Alumina Grinding ceramic pebble