PbO2 Titanium Anode for Hydroxybenzene Wastewater Degradation

Base material

Gr1 titanium as substrate, P_bO₂ as coating

Size

custom-made size available

Coating Thickness

lead oxide (P_bO₂) as coating (8~12um) 

Parameter

Current density≤3000A/M²   

Temperature<60°C

Max content of Fluoride ion is 200PPM

1

High anti-corrosion property

2

High catalytic property

3

High current efficiency property

4

Keep the operating voltage stably

5

High property of current efficiency

6

Decrease the wastage of additive

7

Keep the plating solution stable

8

Long lifetime

9

Different complex geometry design

1

Chromium plating and hard Chromium plating in stronger acid solution

2

Chromate Treatment

3

To make chromic acid; Perchlorate and Periodate

4

Electrochemical oxidation synthetic organic compounds in acid solution

5

Electrolysis recovery and extraction of nonferrous metals in stronger in stronger acid solution

6

Sewage Treatment

1

Low-power current should be galvanized when the anode in the electrolyte

2

No collision

3

No heating

4

Can’t be used as cathode