Specifications
1. Decreasing maintenance cost of equipments2. Reducing energy consumption of mill equipment
3. Improving operation rate
Mining slurry abrasion resistant pipe
Metal content | C:5%,Cr:27-30%,Martensite matrix and Cr7C3 carbides above 60% |
Hardness | Macro hardness of alloy layer HRC57-65, carbide hardness HV1400-1800 |
Wear resistance | 20-25 times than low carbon steel,8-12 times than stainless steel and high manganese steel ,1.5 times than the general chromium carbon steel. |
Temperature resistance | Common lower than 600 degrees; high temperature lower than 1000 degrees |
Impact resistance | Wear resistant alloy layer metallurgically combine with the substrate completely, resistance to strong impact,do not need to worry about shedding |
Workability | Can be welded,cut,folded,drilled |
Specifications
| Name | Mining slurry abrasion resistant pipe |
| Brand | RK |
| Color | brown |
| Diameter | ≥80mm(can be customized) |
| Thickness of wear resistant layer | as customer's require |
| Thickness of pipe wall | 5-30mm |
| Length | can be customized |
| Hardness | HRC57-62 |
| Standard | DIN,GB |
| Certificates | ISO9001:2000 |
| Specifications (base layer+wear resistant layer) | 5+3,6+3,8+3,5+4,6+4,8+4,10+4,6+5,8+5,10+5, 15+5,20+5,6+6,8+6,10+6,20+6,8+8,10+8,10+10, 15+10,20+10 |
| Model number | steel plate Q235 |
| Grade | first class |
| Applications | concrete industry,metallurgy,fan industry,coal industry,mining machinery,construction machinery,etc. |
| Payment terms | L/C,TT,D/P,Western union |
| Delivery time | 15 days after receipt of L/C or advanced payment |
| Trade terms | FOB,CIF,EXW,etc |
| Port | shanghai |