Specifications

Aluminum Strip 5052
Thickness: 0.3-6.0mm
Width: 10-1200mm
ISO9001: 2008,ISO14001:2004,MSDS,SGS

 

Chemical Composition

Cu	0.10
Si+Fe	0.45
Mn	0.10
Mg	2.2/2.8
Zn	0.10
Cr	0.15/0.35
Al	Balance

 

Characteristics

This is a non-heat treatable alloy that is weldable. It is hardened by cold work. It has good forming characteristics and good corrosion resistance, including resistance to salt water.

(1) Machinability
This alloy has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may

(2) Forming
AL 5052 is readily formed at room temperature. Successive cold working decreases the formability.

(3) Corrosion Resistance
Corrosion resistance to salt water and general atmospheric conditions is good.

(4) Welding
This alloy is readily welded by conventional methods. When filler rod is required it should be aluminum alloy 5356 as filler. Either tungsten or consumable electrode inert gas shielded arc welding is preferred method.

(5) Heat Treatment
AL 5052 cannot be hardened by means of heat treatment. It does harden due to cold working.

(6) Forging
The alloy may be forged in the temperature range of 950 F down to 500 F.

(7) Hot Working
Hot working, as with forging, may be done in the range of 950 F to 500 F.

(8) Cold Working
The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.

(9) Annealing
Anneal at 650 F and air cool.

(10) Hardening
Hardens only from cold working. 

(11) Other Physical Props
Electrical conductivity 33% of copper.

(12) Other Mechanical Props
Shear strength for O temper is 18 ksi. For cold worked temper H 34 it is 21 ksi.

Typical Application
Commonly used in the manufacture of hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, and appliances. Commonly used in sheet metal work and in sheet metal parts.

Mechanical Properties

Tensile Strength	196-266MPa
Yield Strength	91-127MPa
Elongation	10-25
Brinell Hardness	47-68