High Quality Two Parts Long Lifetime Liquid Gel Lacquer For Solar Pv Junction Box 

 Features

Room temperature cure or rapid hot cure., solvent-free or byproduct-free ,limited contractility ;

Flame retardant.

Excellent thermal conductive property and dielectric property.

Stable and flexible from -50℃ to 200℃.

Parameters                                                      

Mixing 

The two components should be thoroughly mixed using a weight or volume ratio of 1:1 until the mixture has a uniform color.To make sure the mixture is even,suggest that agitate per A and B respectively before mixing up.Pour the complete mixed material into the target potting side, normally you don’t need to use vacuum to release the bubble, but if high thermal conductivity is needed,suggest that use vacuum at -0.08MPa or above, release the bubble under vacuum environment for about 5-10min first then apply the potting. 

Attention:

1, This produce cure with the help of catalyst platinum, sulfide, nitrogen, sulfur, phosphorus and organic tin compound may inhibit curing process .We suggest that before applying our product ,pls clean the residue of rosin on circuit board and try use low lead solder.
2, choose the room temperature curing process, it is suggested that let the mixture sit still for more than 60 mins to release the bubble before applying in order to obtain the best performances.
3, select heating curing process, it is suggested that the vacuum deaeration, then filling, heat curing, to obtain the best performance.
4, avoid direct contact with epoxy adhesive, polyurethane adhesive, condensation silicone ,which could affect the curing process .

5, should be carried out perfusion within the operating time , base material or electronic components surface should be clean and dry before perfusion .
6, this product is a  non-dangerous goods, but forbid to direct contact with mouth and eyes .

Usable life and storage

Base A and curing agent B has a shelf life of 9 months from the date of manufacture respectively. Pls completely mix the A and B separately before use.