mosi2 industrial heating elements
1.Material:MoSi2
2.Used as heating element
3.Long life,rock bottom price

mosi2 industrial heating elements

We specialize in producing and selling U type molybdenum disilicide,W type molybdenum disilicide,U type right angle Molybdenum disilicide,U type bending molybdenum disilicide,I type molybdenum disilicide,L type molybdenum disilicide,The specification is Φ3,Φ4,Φ6,Φ7,Φ9,Φ10,Φ12.Our product have good reputation at home and abrode.

1) Description

1. General Description: MoSi2 heating element is a resistance generate-heating component made from MoSi2 or the basic material. It is used in high temperature under the oxidizing atmosphere, it looks like glass in its surface and form a light SiO2 glass film which can protect the element not to be oxidized. So this kind of element has unique effect for resisting oxidization in the high temperature. It is used to the highest temperature up to 1800C during oxidizing atmosphere.

2. Specific Properties: low expansion coefficient, little deformation, stable chemical property, long service life, easy installation and maintenance, etc.

3. Characteristics: MoSi2 heating element can usually make use of furnace temperature from 1300C to 1800C. It is used to the highest temperature up to 1800C during oxidizing atmosphere.

4. Application: It is extensively used in the industries of metallurgy, glass, ceramic refractory, crystal electronic device, industrial furnace manufacture, etc.. It is an essential ideal element when the products are sintering in the high temperature.

2) Products specification:

In addition to MoSi2 elements in standard shapes and sizes we provide customed MoSi2 elements according to customer needs, enabling an optimized element design for each particular application.

1. Types: U, W,, rod type. Or special types according to your requirement.

2. Diameter: 3/6 mm, 4/9 mm, 6/12mm, 9/18mm, 12/24mm

3. Temp: 1300-1800 Celsius degrees

Packaging Detail:	outer wooden box, cartoon box inside, polyfoam filled to ensure safety
Delivery Detail	one or two week

3) Technical Data

Density	Bending Strength	Hardness	Apparent Porosity	Water Absorption	Elongation	Fracture Toughness	Compressive Strength
5.8g/cm³	350Mpa	12.0Gpa	±2%	0	4%	4.5Mpa.m1/2	650Mpa

4) The influence of operation temperature on the heater surface in a different atmosphere

Atmosphere	1700 Type	1800 Type
Air	1700	1800
N2	1600	1700
He	1600	1700
-80°C Dry H₂	1150	1150
-20°C Wet H₂	1450	1450
10%CO₂, 50%CO, 15%H₂	1600	1700
40%CO₂, 20%CO	1400	1450
Cracked and Partially Burnt Ammnia	1400	1450

5) MoSi2 heating elements physics and chemistry characters:

1. Physics Characters

Volume Density	Bending Strength	Vickers Hardness	Porosity	Water absorption	Heating Elongation Rate
5.5 g/cm3	15-25 kg/cm3	(HV)570kg/mm2	7.4%	1.2%	4%

2. Chemistry Character
MoSi2 heating element is used in the high temperature under oxidizing atmosphere. It will form the SiO2 film which can keep the element from being melted. During the oxidizing process, the SiO2 protecting film is formed again when the element continues to be used. The MoSi2 heating element must not be used in the temperature between 400C and 700C for a long time, otherwise the element will be cremated under the strong oxidizing function in the low temperature.