Chemical Composition of Stainless Steel 304 and 201

Table 1. Typical chemical composition for 304 stainless steel alloys

%

304

304L

201

C

0-0.07

0-0.03

0.15

Mn

0-2.0

0-2.0

5.50-7.50

Si

0-1

0-1

1.0

P

0-0.05

0-0.05

0.50

S

0-0.02

0-0.02

0.03

Cr

17.5-19.5

17.5-19.5

16.00-18.00

Ni

8-10.5

8-10.5

3.50-5.50

Fe

Balance

Balance

Balance

Properties of Stainless Steel 304

Mechanical Properties of Stainless Steel 304

Grade

304

304L

201

Tensile Strength (MPa)

520-720

500-6070

839

Compression Strength (MPa)

210

-

-

Proof Stress 0.2% (MPa)

210

200

-

Elongation A5 (%)

45 Min

45 Min

50

Hardness Rockwell B

92

-

HRB 94

Physical Properties of Stainless Steel 304

Table 3. Typical physical properties for 304 stainless steel alloys

Property

Value

Density

7.93 g/cm3

7.93 g/cm3

Melting Point

1450°C

Modulus of Elasticity

193 GPa 

29,000,000 psi

Electrical Resistivity

0.072x10-6 Ù.m

Thermal Conductivity

16.2 W/m.K 

Thermal Expansion

17.2x10-6 /K