Specifications

Rotorless rubber rheometer MR-C3
CE certificate
Good repeatability
With computer and printer
Free software updates

Rotorless rubber rheometer MR-C3

Rheometer/Rubber rheometer/moving die rheometer

 

The curves and characteristic parameters on vulcanization of rubber materials can be obtained using rotorless Rheometer based on the measurement of the torque exerted by the rubber material on the oscillating die.
The MR-C3 Rotorless Rheometer has excellent property of reappears and stability. In a test with good mixed rubber and the timerange is 12min, the T90 may be several second difference in 4 continual experiments.

 

Specification:

Items	Specification
Range of temperature control	From room temperature to 200°C
Temperature fluctuation in die	≤±0.1°C
Temperature display resolution	0.1°C
Rate of temperature increase	25°C/min
Measurement range of torque	0-200dNm
Torque resolution	0.01dNm
Angle of die oscillation	±0.5°,±1°,±3
Frequency of die oscillation	1.67Hz (100r/min)

 

Test Results:

·ML Min. torque (dNm)—The testing value of sample’s curing characteristics (viscosity) before curing.

·MH Max. torque (dNm)—The testing value of sample’s shearing modulus or rigidity. Including even torque, max. torque for returning curve, and the max. Torque during the specific period of time where no even or returning curve happens.

·Ts1 (min)— when oscillates at the angle of 0.5° or 1°, the relative time when the torque increases to ML +1dNm. This figure shows the scorch time.

·Ts2 (min)— when oscillates at the angle of 3° or 5°, the relative time when the torque increases to ML +2dNm. This figure shows the scorch time

·T10 (min)—The time when the torque increases to ML + 10 (MH - ML ) / 100dNm. This figure shows the scorch time.

·T30 (min)—The time when the torque increases to ML + 30 (MH - ML ) / 100dNm.

·T60 (min)—The time when the torque increases to ML + 60 (MH - ML ) / 100dNm.

·T90 (min)—The time when the torque increases to ML +90 (MH - ML ) / 100dNm. This figure shows the optimum cure time.

·Ti (min)—The time when the torque increases to ML + i (MH - ML ) / 100dNm.

·Vc—Curing speed index. Vc =100/(T90 – Tsi)

Rotorless rubber rheometer MR-C3

Rheometer/Rubber rheometer/moving die rheometer