Specification

Name: 6000 series Aluminum Plate

Alloy: 6061, 6063, 6082, 6011, 6068 etc.

Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc.

Thickness: 0.2-200mm

Width: up to 1800mm

Length: up to 6000mm

Surface treatment: mill finished, anodized, embossed, PVC coated

Feature

Machinability: It has relatively fair machinability. It is easier to machine in the hard temper than 

as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants 

should be used for machining, except that very light cuts may be done dry.

Forming: It is readily formed at room temperature. Successive cold working decreases the 

formability.

Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold 

working.

Forging: It may be forged in the temperature range of 950 F down to 500 F

Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However 

the amount of cold work imparted by spinning makes intermediate annealing necessary.

Annealing: Anneal at 650 F and air cool.

Hardening: Hardens only from cold working.