Name: Hot sale low thermal conduction ceramic fiber boards
Brand: JIUCHEN
Availability: InStock

Product Details

JIUCHEN Aluminum silicate ceramic fiber board takes ceramic fibers as the main

raw materials ,After fiber processing, slag removing, then add some organicand inorganic

binder, through vacuum forming process, to be made into highstrength fiber board.

Product information

Item	Ceramic fiber board
Type	Standard,High Pure, High Aluminum ,Al-Zirconium,Zirconium.
Classification Temperature	1260°C,1360°C,1430°C
Applications	• Applications that require high-temper, high strength from the load-bearing areas. • For high air flow, mechanical damaging large areas of industrial furnace wall lining, door and roof seals • Construction, fire doors, fire wall fire insulation
Features	• Rigid, free support • Easy to shape or cutting • Acoustic performance • Non-brittle material, good elasticity • Size can be accurate to ± 1mm
Payment Terms	L/C, D/A, D/P, T/T, Western Union, MoneyGram, Cash.
Delivery Time	Within 7-10 days after received the deposit.

ITEM	PRODUCT	COM	STD	HP	HA	HZ
Classification TemperatureºC		1100	1260	1260	1360	1430
Working TemperatureºC		<1000	1050	1100	1200	1350
Color		white	white	white	white	white
Density(kg/m³ )		260 -320	260 - 320	260 - 320	260 - 320	260 320
Liner Shrinkage% (After 24hours)		<2.5	<2.5	<3.5	<2.5	<3.5
Liner Shrinkage% (After 24hours)		1000ºC	1000ºC	(1100ºC)	(1200ºC)	(1350ºC)
Thermal conductivity w/m.k (density128Kg/m3)		0.085 400ºC	0.085 400ºC	0.085 400ºC	0.085 400ºC	0.085 400ºC
		0.132 800ºC	0.132 800ºC	0.132 800ºC	0.132 800ºC	0.132 800ºC
		0.180 (1000ºC)	0.180 (1000ºC)	0.180 (1000ºC)	0.180 (1000ºC)	0.180 (1000ºC)
Tensile strength MPa (Strenth10%)		0.5	0.5	0.5	0.5	0.5
Chemical Composition %	Al₂O₃	44	46	47-49	52-55	39-40
	Al₂O₃+SiO₂	96	97	99	99	-
	Al₂O₃+SiO_{2+ ZrO2}	-	-	-	-	99
	ZrO₂	-	-	-	-	15-17
	Fe₂O₃	<1.2	<1.0	0.2	0.2	0.2
	_Na2O+K2O	≤0.5	≤0.5	0.2	0.2	0.2
Size(mm)	Specification:600X400X10-50,900X600X10-50,other according to customer's requirement