Specifications

1.High refractoriness under load
2.Low reheating liner changing
3.Good performance

  

  

Characteristics

The zirconia bubble brick is made from the bubble zircon and the ZrO2, by adding moderate complex binder, and then through high pressure shape the product. It holds the features below

1.High refractoriness under load

2.Low reheating liner changing

3.Good performance

Application

The bubble zircon brick are mainly used for lining of high temperature furnace and industry ceramic, electrical ceramic, petrochemical and metallurgical industries, as well as the insulation material for super high temperature furnace.

 

The specification of the bubble zirconia brick

Item	Shape-99
Max service temperature	2200
ZrO2% min	99(stabilizer included)
SiO2% max	0.2
Fe2O3% max	0.2
BD (g/cm³)	2.55
CCS(MPa) min	8
RUL (°C)min	1700
PLC % (1600°C×3h)	±0.2
Thermal expansion (×10-6) 1300°C	~9.1
Thermal conductivity w/(m.k) 800°C max	0.3