Modified epoxy grouting material

             Product description:

   Modified epoxy grouting material for the fluid type, cold setting type injection repairing special epoxy grouting material, mainly used for repairing concrete structure crack empty drum, low heat, low shrinkage after hardening, for a variety of structures with very superior to focus on, especially for concrete better then. Through mechanical perfusion (high pressure) or syringe injection method (low pressure), can be further structure is extremely tiny cracks, sufficient to achieve the effect of repair and reinforcement, to restore structure their integrity, and achieve the purpose of the integration.

                 Performance indicators:

Serial number according to the standard inspection items inspection results

1 82 Mpa compressive strength of 40 or higher

2 tensile shear strength 5.0 5.6 Mpa or greater

3 tensile strength 10 15 Mpa or greater

4 bonding strength of dry adhesive 3.0 5.3 Mpa or greater

5 wet viscosity 2.0 5.0 Mpa or greater

6, 300, 333 or higher osmotic pressure than %

             The packing capacity:

The main agent (A) 20 kg / 10 kg

Curing agent (B) 20 kg / 10 kg

Storage stability:

Please do not placed in the high temperature or sun exposure, best in shade. Under normal circumstances, at least a year.

Method:

High pressure or low pressure injection.

Construction than column: A: B = 1:1

             High pressure infusion:

1, the deployment of epoxy, curing agent B, mixing ratio A: B = 1:1 (weight ratio), no need to add any additives or thinner.

2, to make the crack filling completely, should fill in 30 minutes for the second note, when slurry leaking from cracks in the stop.

3, 72 hours after cleaning has solidified epoxy slurry on the lining, pull out the water needle, with polymer waterproof mortar closed hollow.

                       Note:

1, during the period of construction, should avoid contact with skin, must wear gloves, goggles, please rinse with water immediately of any contamination, eyes accidentally touch this product should be hospitalized immediately.

2, the main agent and curing agent must be in accordance with the proportion can stir well before use.

3 mixes, the main agent and curing agent, should be used within the time available to complete, in order to avoid material curing can't use.

4, after use, machinery equipment, scaling, mixer and containers, etc., shall be washed with acetone thoroughly prior to hardening.