Viton Heat Shrink Tubing is made frommodified fluoroelastomer (Viton),
with superior impact, abrasion
Heat Shrink Viton Tubing/shrink sleev e
Description
Viton Heat Shrink Tubing is made from modified fluoroelastomer (Viton), with superior impact, abrasion and cut through resistant, it is suitable to many applications requiring high resistance to corrosive fluids, fuels, lubricants, acids and solvents at elevated temperature.
Features
>Approval: UL, V W-1,
>Meet: SAE-AMS-DTL-23053/13
>Very flexible
>Excellent resistance of chemicals
>Operating temperature -55°C to +200°C
>Minimum fully recovery temperature: 175°C
>Standard color: Black
Technical Data
Property | Test Method | Typical Data |
Operating temperature | IEC 216 | -55°C to +200°C |
Tensile strength | ASTM D 2671 | 8.5MPa |
Elongation at break | ASTM D 2671 | 250% |
Elongation at break after aging | 250°C/168hrs. | 200% |
Heat shock | 300°C/4hrs. | No cracking or dropping |
Flexibility | ASTM D 412 | 13.8MPa |
Flammability | ASTM D 2671 | Self-extinguish in 15sec. |
Volume resistance | ASTM D 876 | 109Ω.cm |
Dielectric strength | ASTM D 2671 | 7.9kV/mm |
Copper corrosion | SAE-AMS-DTL-23053/13 (175°C/16hrs.) | No corrosion |
Specification
Normal size | As supplied(mm) | After recovered (mm) | Tube shape
| Standard length (m/spool) | ||
(inch) | (mm) | Inside diameter (Min.) | Inside diameter (Max.) | Wall thickness (Nom.) | ||
1/8 | 3.2 | 3.2 | 1.6 | 0.76±0.20 | O | 50 |
3/16 | 4.8 | 4.8 | 2.4 | 0.89±0.20 | O | 50 |
1/4 | 6.4 | 6.4 | 3.2 | 0.89±0.20 | O | 50 |
3/8 | 9.5 | 9.5 | 4.8 | 0.89±0.20 | - | 50 |
1/2 | 12.7 | 12.7 | 6.4 | 0.89±0.20 | - | 30 |
3/4 | 19.1 | 19.1 | 9.5 | 1.07±0.30 | - | 30 |
1 | 25.4 | 25.4 | 12.7 | 1.25±0.30 | - | 30 |
1-1/2 | 38.1 | 38.1 | 19.1 | 1.40±0.30 | - | 15 |
2 | 50.8 | 50.8 | 25.4 | 1.65±0.30 | - | 10 |
Remarks:
1. (Viton®) is a registered trademark of E.L Du Pont de Nemours and Co.Inc
2. Tube shape: “O” : Round or Oval, “—”: Flat