zirconia block All-Ceramic Zirconia Block, just as reliable as we always are!
The Zirking All- zirconia furnace Ceramic Zirconia Block is used by dental technician in the lab and millingbcenter and aplying for dental restorations, zirconia all-ceramic crowns and bridges.
²Advantages
Ø Using famous Tosoh Power from Janpan
Ø Excellent translucency
Ø Outstanding Bending Strength
Ø Prefit bio-compatibility
²Size Available for Zirking
| Type | Form(Shape) | Specification | |
| High Translucency | Open system | 98×10mm | 0 step |
| Open system | 98×12mm | 2 steps | |
| Open system | 98×14mm | 2 steps | |
| Open system | 98×16mm | 2 steps | |
| Open system | 98×18mm | 2 steps | |
| Open system | 98×20mm | 2 steps | |
| Zirkconzahn System | 95×16mm | 0 step | |
| Zirkconzahn System | 95×18mm | 0 step | |
| Zirkconzahn System | 95×20mm | 0 step | |
| Zirkconzahn System | 95×22mm | 0 step | |
| High Strength | Open system | 98×10mm | 0 step |
| Open system | 98×12mm | 2 steps | |
| Open system | 98×14mm | 2 steps | |
| Open system | 98×16mm | 2 steps | |
| Open system | 98×18mm | 2 steps | |
| Open system | 98×20mm | 2 steps | |
Element |
% by weight |
ZrO2 |
91-94 |
Y2O3 |
4-6 |
HfO2 |
2-4 |
Al2O3 |
< 0.1 |
SiO2 |
< 0.1 |
Na2O |
< 0.1 |
² Technical Parameters
Description | ISO13356:2008 | High Translucency |
Sintering temp(°C) | / | 1500 |
Sintering Density(g/cm³) | ≥6.0 | 6.01 |
Bending Strength(MPa) | ≥800 | 1200 |
Average grain size(μm) | ≤0.6 | 0.36 |
Translucency | 0.40 | |
Radioactivity(Bp/g) | ≤1.0 | 0.019 |