Geerda K11 Polymer Cement Waterproof Coatings (two-component)
USD $0.5 - $50 /Ton
Min.Order:1 Ton
Foshan Sanshui Xingda Coating Co., Ltd.
PRODUCT DESCRIPTION:
Geerda K11 Flexible waterproof coating is a two-component acrylic polymer modified cement-based waterproof materials. This material is composed of high-grade cement and polymer powder, selected auxiliaries and liquid high-polymer additives. The powder has a active reaction with additives, which, forms a layer of tough, elastic waterproof membrane. This membrane has a good adhesion to concrete and mortar, which, prevents the water from infiltration.
FEATURES:
Ÿ Strong adhesion.
Ÿ Good flexibility & air permeability. .
Ÿ Excellent waterproof performance.
Ÿ Non-toxic, harmless, environment-friendly.
Ÿ Can be paint on the surface of a dry or wet base.
Ÿ Excellent Weather resistance and aging resistance.
Ÿ Can withstand micro-cracks and slight vibration of the building.
RECOMMEND USAGE:
Roof, floor, wall, tunnel, bridges, kitchen, reservoir, basement, bathroom, swimming pool, waterproof construction.
CONSTRUCTION INSTRUCTIONS:
1.Before painting, the surface must be clean, dry, firm and smooth.
2.Construction: Use rubber scraper or roll brush to paint, twice or three times, the coating must be uniform.
3.Before curing, the coating should be well protected, stop treading or putting heavy things on it.
USAGE:
1. Put the powder into liquid container.
2. Fully mixing until there is no precipitation.
3. Keep mixing to avoid precipitation during construction.
Reference Dosage:
Thickness (mm) | 1.2 | 1.5 | 2.0 |
Dosage(Kg/M2) | 2.0-2.3 | 2.6-2.8 | 3.2-3.5 |
Package & Storage
—Package: two-component (Powder + Liquid)
—Store at cool dry place. Avoid direct sunshine and freeze.
Attention
Construction conditions:
Please don’t construct in wet season, rainy season and cold weather (temperature is ≤5°C and humidity is≥85%); otherwise, it will fail to reach the high quality paint film effect that this product should reach.
TECHNICAL INDEX:
Test Item | Index | ||
I | II | ||
Solids content % ≥ | 65 | ||
Drying time H | Surface time ≤ | 4 | |
Completely dry time ≤ | 8 | ||
Tensile strength Mpa ≥ | 1.2 | 1.8 | |
Elongation at break% ≥ | 200 | 80 | |
Wet base surface adhesion strength Mpa ≥ | 0.5 | 1.0 | |
Low temperature flexibility Ø100mm rod | -10°c No cracks | --- | |
Non - permeable 0.3Mpa3min | Impermeable |
Application:
Toilet
Bathroom
Kitchen