hot dip galvanized steel pole clamp
1.standard pole clamp
2.high quality pole clamp
fessional manufacturer

Thank you for you to pay attention to my product ,If you want to know more about ,pls see under; If you have any reuiqres ,pls without hesitate contact me

hot dip galvanized pole clamp

The forged hardware is mainly made of heat treated steel.
This steel is especially suitable for forging and its good performance, especially ductility, is due to the heat treatment process.
The short circuit capability of the Line Hardware fittings depends on the cross sections used as well as the smoothness of bolts and holes and on the mechanical load applied. One should keep in mind that at higher temperatures the strength of the hardware will be reduced.

hot dip galvanized pole clamp

pole clamp is used to the connection of dead-end clamp and suspension clamp with pole or tower

Hot dip galvanized surface treatment, agains rust and corrosion

We design series of fastened fitting for standard pole or tower

The fittings shall be delivered hot dip galvanized according to the following specifications:

The Zinc that shall be used shall have the quality of minimum category prime western according to the category Zn 98.5 according to ISO-1461.
Then washed out with water and then flux treated and dried out.
The hot dip galvanization shall be made in a Zinc bath of temperature 450°C and of Zn-composition min. 98,5%.
The galvanization thickness shall be in average 86μm thick! On an isolated piece or on a small part of the surface the thickness can be a little lower, however on all pieces and on all surfaces the minimum thickness shall be 78μm and the average weight in relation to the galvanized area shall be 610 gr/m2.
The pieces shall be after HDG free from black stains, enclosures of dirt, knobs, bubbles or any other surface defects. The HDG shall be smooth and uniform in the entire piece without any spots with too small or too big galvanization thickness otherwise the pieces will be rejected.
The galvanization shall stick very well on the steel structure; it shall not be removed as a film but shall be as one with the steel body