Zirconium silicate cramic shot peening blasting bead
Negotiable /Kilogram
Min.Order:100 Kilograms
Zibo Qimingxing New Material Co., Ltd.
Zirconium silicate cramic shot peening blasting bead
Ceramic blasting beads are a non-ferrous reusable blasting media with spherical particles.
This blasting media is extremely resistant, and is used above all in applications in which a certain reproducible surface roughness has to be achieved. Ceramic beads are used mainly in the production of foodstuffs
machinery and in the medical field. They represent an alternative to glass beads, with a useful life
which is 8-15 times longer, depending on the application, although this “high
tech” blasting media is extremely expensive, and should therefore only be used in applications
without blasting media loss.
The beads are generally used for surface cleaning of rubber and plastic moulds, castings, boiler and heat exchanger parts. It is also used for the peening and peen forming of components, particularly in the aerospace industry. when used for peening are superior to traditional peening media, like steel shots and glass beads, as it can achieve similar peening intensities with lower surface roughness. can be used in peening applications in the place of steel shots where ferrous contamination is not acceptable.
The higher density of ceramic beads ensures peening intensities equal to those obtainable with glass beads at a reduced abrasive velocity. thus have a far less abrasive breakdown and dust generation which in turn results in a cleaner working environment and better operator visibility. narrow particle size distribution coupled with low breakdown rates up to 15:1 as compared to glass beads enables repeatable, consistent result to be achieved, which is a critical consideration when selecting a media for peening application. Typical applications include mould cleaning, deburring delicate items, peening and stress relieving, deburring plastic components and paint removal.
Technical Data:
|
| Nominal | Measured |
ZrO2 | (wt.-%) | 60-70 | 64.08 |
SiO2 | (wt.-%) | 28-33 | 30.44 |
Al2O3 | (wt.-%) | <10 | 5.77 |
Other constituents | (wt.-%) | <3 | 2.01 |
density | (g/cm³) | 3.6-3.95 | 3.86 |
hardness between 643-785HV | % | >90 | 100 |
Grain size >212um | % | Max.3 | 0 |
Grain size 125-212um | % | Max.10 | 7.58% |
Grain size63-125um | % | Min.80% | 88.74% |
Grain size <63um | % | Max.7% | 3.55% |