Name: LONG ZHONG 2015 ball mill grinding media
Brand: longteng
Availability: InStock

Product Details

LONG ZHONG 2015 ball mill grinding media

ZHANGQIU LONG TENG CEMENT MACHINERY MAKING CO.,LTD is one of biggest manufacturers of cement machinery and relevant spare parts, mainly including Ball Mill, Stone Crusher, Drum Dryer, Reducer, Hot rolled grinding ball, Forged steel ball, Casting grinding ball, Grinding rod, etc.

Our Website:

Product Description

Grinding ball Description:

1) High Hardness: surface hardness of forged and rolling balls is to 60-65 HRC and volume hardness is to 60-63 HRC

2) High Impact Toughness: impact toughness is more than 12 J/cm2;

3) Low Broken Rate: the actual broken rate is not higher than 1%;

4) Even Wear-resistance: the loss of ball round rate is 50-300 g/ton.

Detailed Images

Grinding balls for cement ball mill Picture:

Technical Parameter

Chemical Composition

Based on material, the forged steel balls are defined into 7 brands. And The chemical composition is shown in the following:

Forged Grinding Ball

Brand	Material	C	Mn	Si	Cr	S	P
LT-1	50MN	0.48-0.56	0.70-1.0	0.17-0.37	≤0.25	≤0.035	≤0.035
LT-2	60MN	0.57-0.65	0.70-1.0	0.17-0.37	≤0.25	≤0.030	≤0.030
LT-3	65MN	0.60-0.70	0.90-1.20	0.17-0.37	≤0.25	≤0.030	≤0.030
LT-4	75Mn	0.72-0.92	0.90-1.20	0.17-0.37	≤0.25	≤0.030	≤0.030
LT-5	75MnCr(B2)	0.72-0.85	0.70-1.20	0.17-0.37	0.42-0.85	≤0.030	≤0.030
LT-6	75SiMn	0.70-0.90	0.7-1.2	0.4-0.8	≤0.25	≤0.030	≤0.030
LT-7	B3	0.5-0.65	0.4-1.0	1.4-1.8	0.77-1.10	≤0.030	≤0.030

Casting Grinding Ball

Based on material,the casting steel balls are defined into 6 brands. And The chemical composition is shown in the following:

Name	Model	Material	C	Si	Mn	Cr	S	P
LTC-1	High Chrome	Cr-23-32%	2.0-2.8	≤1.0	0.5-2.0	23-32	≤0.01	≤0.01
LTC-2		Cr-18-22%	2.0-2.8	≤1.0	0.5-2.0	18-22	≤0.01	≤0.01
LTC-3		Cr-15-17%	2.2-3.0	≤1.0	0.5-2.0	15-17	≤0.01	≤0.01
LTC-4		Cr-10-14%	2.2-3.2	≤1.0	0.5-2.5	10-14	≤0.01	≤0.01
LTC-5	Medium Chrome	Cr-5-9%	2.1-3.2	≤1.2	0.5-1.5	5-9	≤0.01	≤0.01
LTC-6	Low Chrome	Cr-1-4%	2.2-3.5	≤1.2	0.5-1.5	1-4	≤0.02	≤0.02