Specifications

Good fluidity
High strength
For brazing of refrigerator and air-condition.

 

 

SPECIFICATIONS:                    CLASSIFICATIONS

AWS  A5.10                          AWS  ER5356

ASME SFA5.10                        UNS  A95356

 

DESCRIPTION

Our ER5356 is a 5% magnesium aluminum filler metal. The weld deposit of this filler metal offers good corrosion resistance when exposed to salt water. This alloy is commonly used on base metals 5050,5052,5083,5356,5454 and 5456. The post-anodizing color tint of the weld area is white.

 

 

TYPICAL MECHANICAL PROPERTIES

Tensile strength:269 MPa

Yield strength:132MPa

Elongation:17%

Melting Point:571-635°C

Processing Temp.:600-645°C

Thermal Conductivity:~100W/m°C

                   27.7%IACS

Electrical Resistivity:~6.0µΩcm

                 ~28%IACS

Welding Process:MIG,TIG

Anodizing: Excellent

Corrosion Resistance: Excellent. Very good in marine atmosphere

Conductivity: Poor

Chemical Composition (%)

Cu1.8-2.2, Mg4.5-5.5,other<0.5, Al:bal.

 

APPLICATION

Parent Metals:5000 series alloys(AlMg) with Mg<4%,6000(AlMgSi) alloys when anodized. Cast alloys of AlSi-Mg type. In practice the most versatile and universally used filler metal.

 

 

ER5356 Aluminum magnesium brazing alloy is a kind of brazing materials containing 5% of magnesium.Featuring high strength, good ductility and excellent corrosion resistance, ER5356 could provide good color for anodized welding. It is widely used for welding or surface build-up brazing of cast-forged aluminum alloys containing 5% of magnesium.