Specifications

Good printability; Distinguished gloss;
High transparency;
Excellent abrasion resistance; Suitable for multiple machines.

Types:

PGLS-20: Printing package foe cigarette.

 

Specification:

Type	Thickness (μm)	Width (mm)	Roll Diameter (mm)
PGLS-20	20 ~23μm	117~1200	200~500

 

Characteristics:

       Good printability.

       Distinguished gloss.

       High transparency.

       Excellent abrasion resistance.

       Good heat shrinkage, specially ideal for tight package contributed to the unique properties of inside surface.

       Low static.

       Perfect surface slip (even in the condition of 60⁰C).

       High stiffness, good foldability.

       Good heat sealability in high speed. 

 

Typical Physical Properties

Items		Methods	Units	PGLS-20
Thickness		GB/T 6672-1986	μm	20.1
Tensile Strength (MD/TD)		GB/T 13022-1991	MPa	192/293
Elongation at Break (MD/TD)		GB/T 13022-1991	%	135/50
Modulus     (MD/TD)		GB/T 13022-1991	MPa	2986/4942
Heat Shrinkage(MD/TD)		120°C×1 min	%	8.9/9.1
Haze		GB/T 2410-1988	%	1.0
Gloss		GB/T 8807-1988	%	96.2
C.O.F	in - in	GB/T 10006-1988	Static/Dynamic	0.43/0.28
	out-out			0.36/0.20
Seal Strength	in - in	135°C×1s×0.18MPa	N/15mm	3.1
	in– out			3.2
	out-out			3.1

Notes:

MD: Machine Direction; TD: Transverse Direction.

The above data can only be regarded as typical physical properties, not guarantee values.

 

Industrial Standards

“Biaxially oriented polypropylene shrink film with both sealable-sides ”.

Foshan Plastics Group Co.,LTD Enterprise Product Standard.

(Standard Code: Q/FS-JS01 15-2006)

 